以硝酸铈和硝酸锆为原料,氨水为沉淀剂,双氧水为氧化剂,采用共沉淀法将铈锆固溶体负载在固态铝源(拟薄水铝石、活性氧化铝和改性氧化铝)表面,制备了铈锆铝复合氧化物.通过XRD,TEM,BET,TPR等手段对铈锆铝复合氧化物进行了结构表征和性能分析.研究结果表明:铈锆固溶体负载在氧化铝上,颗粒明显变小,老化性能得到显著改善;不同形态固态铝源制备的铈错铝复合氧化物性能各异,以拟薄水铝石为铝源制备的样品比表面积最大,以改性氧化铝为铝源制备的样品表现出最佳的储氧性能.
参考文献
| [1] | Matsumoto S .Recent advances in automobile exhaust catalysts[J].Catalysis Today,2004,90:183. |
| [2] | Papavasiliou A;Tsetekou A;Matsouka V;Konsolakis M Yentekakis I V Boukos N .Development of a CeZr-La modified Pt/γ-Al203 TWCs' washcoat:Effect of synthesis procedure on catalytic behavior and thermal durability[J].Applied Catalysis B:Environmental,2009,90:162. |
| [3] | Adamopoulos O;Bj(o)rkman E;Zhang Y;Muhammed M Bog T Mussmann L Lox E .A nanophase oxygen storage material:Alumina-coated metal-based ceria[J].J Eur Ceram Soe,2009,29:677. |
| [4] | Shinjoh H .Rare earth metals for automotive exhaust catalysts[J].Journal of Alloys and Compounds,2006,408-412:1061. |
| [5] | Wang J Q;Shen M Q;An Y;Wang J .Ce-Zr-Sr mixed oxide prepared by the reversed microemulsion method for improved Pd-only three-way catalysts[J].CATALYSIS COMMUNICATIONS,2008,10:103. |
| [6] | Li G F;Wang Q Y;Zhao B;Zhou R X .A new insight into the role of transition metals doping with CeO2-ZrO2 and its application in Pd-only three-way catalysts for automotive emission control[J].FUEL,2012,92:360. |
| [7] | Raju V;Jaenicke S;Chuah G K .Effect of hydrothermal treatment and silica on the thermal stability and oxygen storage capacity of ceria-zirconia[J].Applied Catalysis B:Environmental,2009,91:92. |
| [8] | 李彦英,郭耘,卢冠忠,郭杨龙,张志刚.铋杂对Ce-Zr固溶体储氧性能稳定性的影响[J].中国稀土学报,2010(04):408-413. |
| [9] | 洪燕霞,梁红,李树华,王婷婷.钾元素掺杂对铈锆固溶体中氧物种的影响[J].中国稀土学报,2012(04):429-435. |
| [10] | Morikawa A;Suzuki T;Kanazawa T;Kikuta K;Suda A;Shinjo H .A new concept in high performance ceria-zirconia oxygen storage capacity material with Al2O3 as a diffusion barrier[J].Applied Catalysis, B. Environmental: An International Journal Devoted to Catalytic Science and Its Applications,2008(3/4):210-221. |
| [11] | Chuang C C;Hsiang H I;Hwang J S;Wang T S .Synthesis and characterization of Al2O3-Ce0.5Zr0 5O2 powders prepared by chemical coprecipitation method[J].Journal of Alloys and Compounds,2009,470:387. |
| [12] | Li H M;Zhu Q C;Li Y L;Gong M C Chen Y D Wang J L Chen Y Q .Effect of ceria/zirconia ratio on properties of mixed CeO2-ZrO2-Al2O3 compound[J].Journal of Rare Earths,2010,28:79. |
| [13] | 韩毅,史运宝,马新胜,高玮.不同铝源与铈锆复合的性能及机制[J].中国稀土学报,2013(02):222-227. |
| [14] | Kaspar J.;Fornasiero P. .Nanostructured materials for advanced automotive de-pollution catalysts[J].International Journal of Quantum Chemistry,2003(1/2):19-29. |
| [15] | Ozawa M .Thermal stabilization of catalytic compositions for automobile exhaust treatment through rare earth modification of alumina nanoparticle support[J].Journal of Alloys and Compounds,2006,408-412:1090. |
| [16] | Suda A;Yamamura K;Ukyo Y;Sasaki T Sobukawa H Tanabe T Nagai Y Sugiura M .Effect of specific surface area of ceria-zirconia solid solution on their oxygen storage capacity[J].Journal of the Ceramic Society of Japan,2004,112:581. |
| [17] | Yu Q;Wu X X;Yao X J;Liu B Gao F Dong L .Mesoporous ceria-zirconia-alumina nanocomposite-supported copper as superior catalyst for simultaneous catalytic elimination of NO-CO[J].CATALYSIS COMMUNICATIONS,2011,12:1311. |
| [18] | Liotta L F;Macaluso A;Longo A;Pantaleo G Martorana A Deganello G .Effect of redox treatments on the structural composition of a ceria-zirconia oxide for application in the three-way catalysis[J].Applied Catalysis A:General,2003,240:295. |
| [19] | Fornasiero P;Balducci G;Dimonte R;Ka(s)par J Sergo V Gubitosa G Ferrero A Graziani M .Modification of the redox behavior of CeO2 induced by structural doping with ZrO2[J].Journal of Catalysis,1996,164:173. |
| [20] | Morikawa A;Kikuta K;Suda A;Shinjo H .Enhancement of oxygen storage capacity by reductive treatment of Al2O3 and CeO2-ZrO2 solid solution nanocomposite[J].Applied Catalysis B:Environmental,2009,88:542. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%