A silicon (Si) surface with a nanosized porous structure was formed via simple wet chemical etching catalyzed by gold (Au) nanoparticles on p-type Cz-Si (100).The average reflectivity from 300 to 1200 nm was less than 1.5％.Black Si solar cells were then fabricated using a conventional production process.The results reflected the output characteristics of the cells fabricated using different etching depths and emitter dopant profiles.Heavier dopants and shallower etching depths should be adopted to optimize the black Si solar cell output characteristics.The efficiency at the optimized etching time and dopant profile was 12.17％.However,surface passivation and electrode contact due to the nanosized porous surface structure are still obstacles to obtaining high conversion efficiency for the black Si solar cells.
参考文献
| [1] | Branz H M,Yost V E,Ward S,et al.Nanostructured black silicon and the optical reflectance of graded-density surfaces.Appl Phys Lett,2009,94(23): 231121 |
| [2] | Li X,Bohn P W.Metal-assisted chemical etching in HF/H-2O2 produces porous silicon.Appl Phys Lett,2000,77(16): 2572 |
| [3] | Sai H,Fujii H,Arafune K,et al.Wide-angle antireflection effect of subwavelength structures for solar cells.Jpn J Appl Phys Part 1-Regular Papers Brief Communications & Review Papers,2007,46(6A): 3333 |
| [4] | Koynov S,Brandt M S,Stutzmann M.Black nonrefiecting silicon surfaces for solar cells.Appl Phys Lett,2006,88(20): 203107 |
| [5] | Koynov S,Btandt M S,Stuzmann M.Black multi-crystalline silicon solar cells.Phys Status Solidi R,2007,1(2): R53 |
| [6] | Tsujino K,Matsumura M,Nishimoto Y.Texturization of multicrystalline silicon wafers by chemical treatment using metallic catalyst.Proceedings of 3rd World Conference on Photovoltaic Energy Conversion,2003,2:1507 |
| [7] | Srivastava S K,Kumar D,Vandana,et al.Silver catalyzed nanotexturing of silicon surfaces for solar cell applications.Solar Energy Materials & Solar Cells,2012,100:33 |
| [8] | Nishioka K,Horita S.Nano-sized taper structure formed by wet process using catalysis of gold nanoparticle.MRS Proceedings,2007,1059E: 1059-kk09-07 |
| [9] | Xiu Y,Hess D W,Wong C P.Herarchically etched silicon lotus effect surface structures for reduced light reflection.Electronics Packaging Technology Conference,2008,9:916 |
| [10] | Roucous A,Schulz J,Patin H.Reduced transition metal colloids:a novel family of reusable catalysts.Chem Rev,2002,102(10):3757 |
| [11] | Chen C,Kuo P.Gold nanoparticles prepared using polyethylenimme adsorbed omo montmorillonite.Journal of Colloid and Interface Science,2006,293(1): 101 |
| [12] | Schulz J,Roucoux A,Patin H.Stabilized hodium(0) nanoparticles: a reusable hydrogenation catalyst for arene derivatives in a biphasic water-liquid system.Chemistry—A European Journal,2000,6(4): 618 |
| [13] | Sun X,Dong S,Wang E.One-step polyeleetrolyte-based route to well-dispersed gold nanoparticles: synthesis and insight.Mater Chem Phys,2006,96(1): 29 |
| [14] | Yuan H C,Yost V E,Page M R,et al.Efficient black silicon solar cells with nanoporous anti-reflection made in a single-step liquid etch.34th IEEE Photovoltaic Specialists Conference,2009:000141 |
| [15] | Nishioka K,Sueto T,Saito N.Antireflection structure of silicon solar cells formed by wet process using catalysis of single nanosized gold or silver particle.34th IEEE Photovoltaic Specialists Conference,200:169 |
| [16] | Nishioka K,Sueto T,Saito N.Formation of antireflection nanostructure for silicon solar cells using catalysis of single nanosized silver particle.Appl Surf Sci,2009,255(23): 9504 |
| [17] | Nishioka K,Horita S,Ohdaira K,et al.Antireflection subwave-length structure of silicon surface formed by wet process using catalysis of single nano-sized gold particle.Solar Energy Materials & Solar Cells,2008,92(8): 919 |
| [18] | Yuan H C,Yost V E,Page M R,et al.Efficient black silicon solar cell with a density-graded nanoporous surface-optical properties-performance limitations-and design rules.Appl Phys Lett,2009,95(12): 123501 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%