Ti/WSi/Ni contact to n-type SiCN was investigated using the circular transmission line method. Current-voltage characteristics, X-ray diffraction and X-ray photoelectron spectroscopy were used to characterize the contacts before and after annealing. It is shown that the conducting behavior of the contacts is dependent on the annealing temperature. After annealing at 900 ℃ or above, ohmic contacts with specific contact resistivity were achieved. The 1000-℃-annealed contact exhibits the lowest specific contact of 3.07 ×10-5 Ω·cm2. The formation of ohmic contact with low specific contact resistivity was discussed.
参考文献
| [1] | Chen L C,Chen C K,Wei S L,et al.Crystalline silicon carbon nitride:a wide band gap semiconductor.Appl Phys Lett,1998,72:2463 |
| [2] | Chang H L,Kuo C T.Properties of Si-C-N films prepared on Si substrate using cobalt interfacial layers.Mater Chem Phys,2001,72:236 |
| [3] | Bhusari D M,Chen C K,Chen K H,et al.Composition of SiCN crystals consisting of a predominantly carbon-nitride network.J Mater Res,1997,12:322 |
| [4] | Badzian A,Badzian T,Drawl W D,et al.Silicon carbonitride:a rival to cubic boron nitride.Diamond Relat Mater,1998,7:1519 |
| [5] | Chang H L,Kuo C T.Characteristics of Si-C-N films deposited by microwave plasma CVD on Si wafers with various buffer layer materials.Diamond Relat Mater,2001,10:1910 |
| [6] | Komateu S,Hirohata Y,Fukuda S,et al.Preparation and characterization of reactively sputtered SiCχNy films.Thin Solid Films,1990,193/194:917 |
| [7] | Novikov N V,Voronkin M A,Zaika N I.Mechanical properties of thin ceramic coatings of the Si=C=N system deposited by reactive ion-plasma sputtering.Diamond Relat Mater,1992,1:580 |
| [8] | Uslu C,Park B,Poker D B.Synthesis of metastable carbon-silicon-nitrogen compounds by ion implantation.J Electron Mater,1996,25:23 |
| [9] | Liew L A,Zhang W,Bright V M,et al.Fabrication of SiCN ceramic MEMS using injectable polymer-precursor technique.Sensors and Actuators A,2001,89:64 |
| [10] | Liew L A,Liu Y,Luo R,et al.Fabrication of SiCN MEMS by photopolymerization of pre-ceramic polymer.Sensors and Actuators A,2002,95:120 |
| [11] | Liu Y,Liew L A,Luo R,et al.Application of microforging to SiCN MEMS fabrication.Sensors and Actuators A,2002,95:143 |
| [12] | Gregori G,Kleebe H J,Brequelet H,et al.Microstructure evolution of precursors-derived SiCN ceramics upon thermal treatment between 1000 and 1400 ℃.Journal of Non-Crystalline Solids,2005,351:1393 |
| [13] | Barbadillo L,Gomez F J,Hernandez M J,et al.Nitrogen incorporation in amorphous SiCN layers prepared from electron cyclotron resonance plasmas.Appl Phys A,1999,68:603 |
| [14] | Nakaaki I,Saito N.Optical,electrical and structural properties of amorphous SiCN:H films prepared by RF glow-discharge decomposition.Appl Surf Sci,2001,169/170:468 |
| [15] | Chou Y C,Chattopadhyay S,Chen L C,et al.Doping and electrical properties of amorphous silicon carbon nitride films.Diamond and Related Materials,2003,12:1213 |
| [16] | Probst D,Hoche H,Zhou Y,et al.Development of PE-CVD Si/CN:H films for tribological and corrosive complex-load conditions.Surface and Coating Technology,2005,200:355 |
| [17] | Chang W R,Fang Y K,Ting S F,et al.The contact characteristics of SiCN films for opto-electrial devices applications.J Electron Mater,2004,33:181 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%