采用一种不含有机溶剂的聚酰胺酸上浆剂实施上浆处理,为在T300级炭纤维(3 k)表面制备聚酰亚胺( PI)涂层提供一种绿色途径。通过傅里叶变换红外光谱和扫描电子显微镜对PI涂覆炭纤维的表面进行分析,结果表明,在炭纤维表面形成一层连续且均一的PI涂层。通过热重分析和单丝拉伸测试,考察炭纤维的热稳定性。与包含环氧上浆剂的炭纤维相比,在耐高温树脂的加工温度范围(300~400℃)内PI涂覆炭纤维表现出优异的热稳定性,起始分解温度与5%热失重温度分别高达567℃及619℃。此外,在空气中、400℃条件下氧化1 h后,PI涂覆炭纤维的拉伸强度仅下降6%,明显低于包含环氧上浆剂炭纤维(拉伸强度下降22%)。
Organic, solvent-free polyamic acid sizing was coated onto T300 grade carbon fibers (3k) to prepare a polyimide (PI) coating having a high thermal stability and oxidative resistance. The surface of PI-coated carbon fibers was characterized by FTIR and SEM. The mechanical strength of the carbon fibers, thermal stability and oxidative resistance of the coating were also investiga-ted. Results indicate that a continuous and uniform PI coating is formed on the surface of the carbon fibers. Compared to a carbon fiber coating with epoxy, the PI coating produces excellent thermal stability with onset decomposition and a 5% weight-loss tempera-tures of 567 and 619 ℃, respectively. The tensile strength of PI-coated carbon fibers after thermal oxidation in air at 400 ℃ for 1 h has only a slight decrease of 6%, which is significantly lower than the decrease of 22% for epoxy-coated fibers.
参考文献
| [1] | Li, W.;Long, D.;Miyawaki, J.;Qiao, W.;Ling, L.;Mochida, I.;Yoon, S.-H. .Structural features of polyacrylonitrile-based carbon fibers[J].Journal of Materials Science,2012(2):919-928. |
| [2] | Li M;Gu Y Z;Liu Y N et al.Interfacial improvement of car-bon fiber/epoxy composites using a simple process for depositing commercially functionalized carbon nanotubes on the fibers[J].CARBON,2013,52:109-121. |
| [3] | Kenneth C. Cheung;Neil Gershenfeld .Reversibly Assembled Cellular Composite Materials[J].Science,2013(Sep.19 TN.6151):1219-1221. |
| [4] | Tong Yuanjian;Wang Xiaoqian;Su Hua;Xu Lianghua .Oxidation kinetics of polyacrylonitrile-based carbon fibers in air and the effect on their tensile properties[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2011(8):2484-2488. |
| [5] | Zhang R L;Huang Y D;Liu L et al.Effect of the molecular weight of sizing agent on the surface of carbon fibres and inter-face of its composites[J].Applied Surface Science,2011,257(6):1840-1844. |
| [6] | U. K. Vaidya;K. K. Chawla .Processing of fibre reinforced thermoplastic composites[J].International Materials Reviews,2008(4):185-218. |
| [7] | Haojie Yuan;Shouchun Zhang;Chunxiang Lu;Shuqing He;Feng An .Improved interfacial adhesion in carbon fiber/polyether sulfone composites through an organic solvent-free polyamic acid sizing[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013(Aug.15):279-284. |
| [8] | Mohit Sharma;Jayashree Bijwe .Influence of fiber-matrix adhesion and operating parameters on sliding wear performance of carbon fabric polyethersulphone composites[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2011(11/12):2919-2927. |
| [9] | ZhishuangDai;Fenghui Shi;BaoyanZhang;MinLi;ZuoguangZhang .Effect of sizing on carbon fiber surface properties and fibers/epoxy interfacial adhesion[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2011(15):6980-6985. |
| [10] | 杨禹,吕春祥,王心葵,刘鸿鹏,贺福,李永红,宋燕.纳米SiO2改性上浆剂对炭纤维复合材料界面性能的影响[J].新型炭材料,2005(03):211-216. |
| [11] | Kedong Xia;Chunxiang Lu;Yu Yang .Preparation of anti-oxidative SiC/SiO_2 coating on carbon fibers from vinyltriethoxysilane by sol-gel method[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013(Jan.15):603-609. |
| [12] | M. Das;J. Ghosh;A.K. Basu .Effect of activation on boron nitride coating on carbon fiber[J].CERAMICS INTERNATIONAL,2010(8):2511-2514. |
| [13] | Emig G.;Schoch G.;Stumm T.;Popovska N. .The coating of continuous carbon fiber bundles with SiC by chemical vapor deposition: A mathematical model for the CVD-process[J].Carbon: An International Journal Sponsored by the American Carbon Society,1998(4):407-415. |
| [14] | Li XK;Dong ZJ;Westwood A;Brown A;Zhang SW;Brydson R;Li N;Rand B .Preparation of a titanium carbide coating on carbon fibre using a molten salt method[J].Carbon: An International Journal Sponsored by the American Carbon Society,2008(2):305-309. |
| [15] | Amit K. Roy;Steffen Schulze;Michael Hietschold .Oxidation protection of carbon fibers by coating with alumina and/or titania using atomic layer deposition[J].Carbon: An International Journal Sponsored by the American Carbon Society,2012(3):761-770. |
| [16] | 吕晓轩,吕春祥,杨禹,周普查,安锋,贺福.阳极氧化对炭纤维电镀镍的影响[J].新型炭材料,2010(06):454-459. |
| [17] | Sause, MGR;Haider, F;Horn, S .Quantification of metallic coating failure on carbon fiber reinforced plastics using acoustic emission[J].Surface & Coatings Technology,2009(3):300-308. |
| [18] | X.H. Zheng;Y.G. Du;J.Y. Xiao;W.J. Zhang;L.C. Zhang .Double Layer Oxidation Resistant Coating For Carbon Fiber Reinforced Silicon Carbide Matrix Composites[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2009(7):4250-4254. |
| [19] | Isabelle Giraud;Sophie Franceschi-Messant;Emile Perez;Colette Lacabanne;Eric Dantras .Preparation of aqueous dispersion of thermoplastic sizing agent for carbon fiber by emulsion/solvent evaporation[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2013(Feb.1):94-99. |
| [20] | M.Hasegawa;K.Horie .Photophysics,photochemistry,and optical properties of polyimides[J].Progress in Polymer Science,2001(2):259-335. |
| [21] | 曹霞,温月芳,张寿春,杨永岗.耐温型炭纤维乳液上浆剂[J].新型炭材料,2006(04):337-342. |
| [22] | The effect of a compliant polyimide nanocoating on the tensile properties of a high strength PAN-based carbon fiber[J].Composites science and technology,2009(7/8):1319-1322. |
| [23] | Putkonen M;Harjuoja J;Sajavaara T;Niinisto L .Atomic layer deposition of polyimide thin films[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2007(7):664-669. |
| [24] | Cho D;Choi Y;Chang JH;Drzal LT .Interphase sizing temperature effect of LaRC PETI-5 on the dynamic mechanical thermal properties of carbon fiber/BMI composites[J].Composite interfaces,2006(2/3):215-229. |
| [25] | Chuang S L;Chu N J;Whang W T .Effect of polyamic acids on interfacial shear strength in carbon fiber/aromatic thermo-plastics[J].Journal of Appllied Polymer Science,1990,41(1-2):373-382. |
| [26] | 安锋,吕春祥,郭金海,和树庆,卢慧斌,杨禹.碳纳米管接枝炭纤维对环氧树脂浸润性能的影响[J].新型炭材料,2011(05):361-367. |
| [27] | Shin S.;Yoon SH.;Mochida I.;Jang J. .A STUDY ON THE EFFECT OF HEAT TREATMENT ON FUNCTIONAL GROUPS OF PITCH BASED ACTIVATED CARBON FIBER USING FTIR[J].Carbon: An International Journal Sponsored by the American Carbon Society,1997(12):1739-1743. |
| [28] | Tamaki Naganuma;Kimiyoshi Naito;Jenn-Ming Yang .High-temperature vapor deposition polymerization polyimide coating for elimination of surface nano-flaws in high-strength carbon fiber[J].Carbon: An International Journal Sponsored by the American Carbon Society,2011(12):3881-3890. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%