将聚丙烯腈基炭纤维在石墨化炉中维持定长加热，以模拟炭/炭复合材料制备过程中炭纤维结构的变化，并采用小角X射线散射( SAXS)和高分辨透射电子显微镜( HRTEM)检测石墨化过程中的结构演变。随着温度的提高炭纤维中微孔的平均回转半径、长度、宽度、截面积和体积分数呈现先减小后增大的趋势，并在约2300益出现极小值。炭纤维中孔隙尺寸的变化与炭层片的活动性密切相关。炭层的缩合和有序化导致孔隙率的减小，而炭层在更高温的簇状化导致孔隙尺寸的增大。
Polyacrylonitrile-based carbon fiber bundles, with two sides fixed, were heated in a graphitization furnace with temper-ature profiles similar to those used in the preparation of carbon/carbon composites. The microstructure of the microvoids formed was characterized by small-angle X-ray scattering and high resolution transmission electron microscopy ( HR-TEM) . Results showed that the average radius of gyration of the microvoids decreases, and their length, width, cross-sectional area and volume fraction de-crease followed by a slight increase with increasing temperature, with the minima found at around 2300℃. The HR-TEM images showed that the microvoids were formed by stacking defects of the carbon layers. The ordering of the amorphous carbon layers ac-counted for the initial decrease of size and volume fraction of the voids with increasing temperature, while the growth and ordering of the layers at high temperatures gave rise to increases in their size and volume fraction.
参考文献
| [1] | Wang P;Zhang S;Li H et al.Variation of thermal expan-sion of carbon/carbon composites from 850 to 2500℃[J].Ce-ram Intern,2014,40:1273-1276. |
| [2] | 孙超,张博,杨晓光,许正辉,宋怀河,花双平,陈晓红.原位聚合增密次数对C/C复合材料性能的影响[J].新型炭材料,2012(01):49-54. |
| [3] | 付前刚,薛晖,李贺军,李克智,史小红,赵华.多涂层炭/炭复合材料抗1500℃燃气冲刷性能的研究[J].新型炭材料,2010(04):279-284. |
| [4] | White JDE;Simpson AH;Shteinberg AS;Mukasyana AS .Combustion joining of refractory materials: Carbon-carbon composites[J].Journal of Materials Research,2008(1):160-169. |
| [5] | Kulkarni M R;Brady R P .A model of global thermal conductiv-ity in laminated carbon/carbon composites[J].Computer Science & Technology,1997,57(03):277-285. |
| [6] | Sauder C;Lamon J;Pailler R .The tensile behavior of carbon fi-bers at high temperatures up to 2400℃[J].CARBON,2004,42(04):715-725. |
| [7] | Xu Z;Liu L;Huang Y et al.Graphitization of polyacrylonitrile carbon fibers and graphite irradiated by γ rays[J].Materials Letters,2009,63:1814-1816. |
| [8] | Watanabe T;Ohtsuka Y;Nishiyama Y .Nitrogen removal and carbonization of polyacrylonitrile with ultrafine metal particles at low temperatures[J].CARBON,1994,32(02):329-334. |
| [9] | A. TAKAKU;M. SHIOYA;T. MANGANZI .The application of temperature-time superposition to the study of structural development in the heat-treatment of carbon fibers[J].Carbon: An International Journal Sponsored by the American Carbon Society,1996(11):1449-1452. |
| [10] | Moreton R;Watt W;Johnson W .Carbon fibers of high strength and high breaking strain[J].NATURE,1967,213(5077):690-691. |
| [11] | Wu, G.-P.;Li, D.-H.;Yang, Y.;Lu, C.-X.;Zhang, S.-C.;Li, X.-T.;Feng, Z.-H.;Li, Z.-H. .Carbon layer structures and thermal conductivity of graphitized carbon fibers[J].Journal of Materials Science,2012(6):2882-2890. |
| [12] | Crawshaw J. .A small angle X-ray scattering study of pore structure in Tencel cellulose fibres and the effects of physical treatments[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(12):4691-4698. |
| [13] | Cohaut N;Guet J M;Diduszko R .SAXS investigations on the porosity of pitch based carbon fibers[J].CARBON,1996,34(05):674-676. |
| [14] | Shioya M;Takaku A .Characterization of microvoids in polyac-rylonitrile-based carbon fibers[J].Journal of Applied Physics,1985,58:4074-4082. |
| [15] | Harris PJF;Tsang SC .High-resolution electron microscopy studies of non-graphitizing carbons[J].Philosophical Magazine.A.Physics of condensed matter, defects and mechanical properties,1997(3):667-677. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%