Ultrafine austenite grains (UFAGs) with size of 1-5 μm were prepared through repet-itive treatment, four times, of rapid heating and quenching, and the growth behaviors of these UFAGs during both the reheating and cooling stages were investigated. The results indicated that UFAGs without pinning particles appeared with significant coarsening when the reheating temperature reached 1000 °C. Although coarsening still occurred in the cooling stage, the growth was obscured during the isothermal holding process at temperatures between 900 °C and Ar3.
参考文献
| [1] | J Huang;Z Xu .[J].Materials Letters,2006,60:1854. |
| [2] | V V Sagaradze .[J].Nano-Structured Materials,1997,9:201. |
| [3] | Y Kimura;S Takagi;S Tcrasaki.[A].Korea Institute of Metals and Materials Press,Pohang,Korea,2002 |
| [4] | G X Liu.Principle of Metals[M].北京:冶金工业出版社,1983:308. |
| [5] | J Moon;I Lee;C Lee .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,459:40. |
| [6] | S Renata;A Henryk;A Anna .[J].Mater Charuct,2006,56:340. |
| [7] | C G Xu;Y G Tian .[J].Spec Stell,1995,16:19. |
| [8] | L X Du;M X Xiong;S J Yao;X.H.Liu and G.D.Wang .[J].Acta MetaU Sin,2007,43:59. |
| [9] | S Uhm;J Moon;C Lee;J.Yoon and B.Lee .[J].ISIJ International,2004,44:1230. |
| [10] | R A Vanderrneer;Ⅱ Hu .[J].Acta MetaU Mater,1994,42:3071. |
| [11] | C S Smith .[J].7'rans AIME,1949,175:15. |
| [12] | J J Qi;Y H ttuang;Y Zhang.Microalloyed Steel[M].北京:冶金工业出版社,2006:33. |
| [13] | Z Li .[D].沈阳:东北大学,2000. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%