采用摩擦失重法、电化学测试以及扫描电子显微镜等技术研究 TC4钛合金在模拟海水环境中的腐蚀和腐蚀磨损行为，分析电化学状态对 TC4钛合金钝化行为、钝化膜失效机制及腐蚀磨损协同作用的影响。结果表明，摩擦过程中 TC4钛合金的开路电位明显负移，而且该合金的腐蚀电流密度相比静态腐蚀时提高了3个数量级。合金的腐蚀磨损失重随着电位的升高明显增大，磨蚀与磨损之间存在明显的协同作用，高电位时的腐蚀速度较大但是摩擦因数较低。电位在 OCP 和0.9 V 之间变化时，纯机械磨损量在总腐蚀磨损量中的比重随着电位的升高逐渐降低，而磨损对腐蚀的促进量和腐蚀对磨损的促进量在总腐蚀磨损量中的比重在高电位时尤其显著。
The electrochemical and corrosion?wear behaviors of TC4 alloy in artificial seawater were studied. And the influences of electrochemical state on passive behavior, failure mechanism of passive film and corrosion?wear synergy were emphatically analyzed. The corrosion?wear analysis of the alloy was fulfilled by methods of mass loss, electrochemical testing and scanning electron microscope (SEM). It can be observed that the cathodic shift of open circuit potential and three order of magnitude increase of current density can be obtained during corrosion?wear process. Total corrosion?wear loss increases with increasing applied potential, confirming the synergy between wear and corrosion. High polarisation potential results in low coefficient of friction and high corrosion rate. The relative contribution of pure mechanical wear to total material loss deceases obviously with the increase of potential from open circuit potential to 0.9 V during corrosion?wear. Contributions of wear-induced-corrosion and corrosion-induced-wear are significant especially at higher potentials.
参考文献
| [1] | 陈君;阎逢元.Ti-6Al-4V和Monel K500合金在海水环境中与316不锈钢对磨时的腐蚀磨损性能[J].中国有色金属学报（英文版）,2012(6):1356-1365. |
| [2] | Hongyan Ding;Zhendong Dai;Fei Zhou;Guanghong Zhou.Sliding friction and wear behavior of TCI 1 in aqueous condition[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20071/6(1/6):117-124. |
| [3] | 陈君;王建章;阎逢元;张清;李全安.Hastelloy C276合金在模拟海水环境中的腐蚀磨损协同作用[J].中国有色金属学报（英文版）,2015(2):661-668. |
| [4] | S. Hiromoto;S. Mischler.The influence of proteins on the fretting-corrosion behaviour of a Ti6Al4V alloy[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20069(9):1002-1011. |
| [5] | I. Serre;R. M. Pradeilles-Duval;N. Celati.Tribological and corrosion experiments of graphite ring against Ti-6Al-4V disk: Influence of electrochemical and mechanical parameters[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20069/10(9/10):1129-1135. |
| [6] | M. M. Stack;J. Rodling;M. T. Mathew;H. Jawan;W. Huang;G. Park;C. Hodge.Micro-abrasion-corrosion of a Co-Cr/UHMWPE couple in Ringer's solution: An approach to construction of mechanism and synergism maps for application to bio-implants[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20105/6(5/6):376-382. |
| [7] | CHEN JUN;YAN FENGYUAN.Corrosive Wear Performance of Monel K500 Alloy in Artificial Seawater[J].Tribology Transactions,20135(5):848-856. |
| [8] | N. Espallargas;R. Johnsen;C. Torres;A. I. Munoz.A new experimental technique for quantifying the galvanic coupling effects on stainless steel during tribocorrosion under equilibrium conditions[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20131/2(1/2):190-197. |
| [9] | Liu, J.;Wang, X.;Wu, B.J.;Zhang, T.F.;Leng, Y.X.;Huang, N..Tribocorrosion behavior of DLC-coated CoCrMo alloy in simulated biological environment[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2013:39-43. |
| [10] | Stefano Mischler;Anna Igual Munoz.Wear of CoCrMo alloys used in metal-on-metal hip joints: A tribocorrosion appraisal[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20131/2(1/2):1081-1094. |
| [11] | E. Boese;J. Rothig;I. Garz;H. Schmidtchen.Tribocorrosion of stainless steels[J].Materials and Corrosion,19982(2):98-107. |
| [12] | M. T. Mathew;E. Ariza;L. A. Rocha;F. Vaz;A. C. Fernandes;M. M. Stack.Tribocorrosion behaviour of TiC_xO_y thin films in bio-fluids[J].Electrochimica Acta,20102(2):929-937. |
| [13] | Mathew,M.T.;Nagelli,C.;Pourzal,R.;Fischer,A.;Laurent,M.P.;Jacobs,J.J.;Wimmer,M.A..Tribolayer formation in a metal-on-metal (MoM) hip joint: An electrochemical investigation[J].Journal of the mechanical behavior of biomedical materials,2014:199-212. |
| [14] | P. Henry;J. Takadoum;P. Bercot.Tribocorrosion of 316L stainless steel and TA6V4 alloy in H_2SO4_ media[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,20096(6):1308-1314. |
| [15] | P. Henry;J. Takadoum;P. Bercot.Depassivation of some metals by sliding friction[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,20111(1):320-328. |
| [16] | S. Barril;S. Mischler;D. Landolt.Electrochemical effects on the fretting corrosion behaviour of Ti6Al4V in 0.9% sodium chloride solution[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20051(1):282-291. |
| [17] | R. Priya;C. Mallika;U. Kamachi Mudali.Wear and tribocorrosion behaviour of 304L SS, Zr-702, Zircaloy-4 and Ti-grade2[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20141/2(1/2):90-100. |
| [18] | K. C. Tekin;U. Malayoglu.Assessing the Tribocorrosion Performance of Three Different Nickel-Based Superalloys[J].Tribology letters,20103(3):563-572. |
| [19] | A. Iwabuchi;J. W. Lee;M. Uchidate.Synergistic effect of fretting wear and sliding wear of Co-alloy and Ti-alloy in Hanks' solution[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20071/6(1/6):492-500. |
| [20] | P. Ponthiaux;R Wenger;D. Drees;J. P. Celis.Electrochemical techniques for studying tribocorrosion processes[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20045(5):459-468. |
| [21] | N. Diomidis;J.-P. Celis;P. Ponthiaux;F. Wenger.Tribocorrosion of stainless steel in sulfuric acid: Identification of corrosion-wear components and effect of contact area[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20101/2(1/2):93-103. |
| [22] | M. Salasi;G. B. Stachowiak;G. W. Stachowiak.New Experimental Rig to Investigate Abrasive-Corrosive Characteristics of Metals in Aqueous Media[J].Tribology letters,20101(1):71-84. |
| [23] | Mischler S.;Stemp M.;Landolt D.;Spiegel A..Influence of passivity on the tribocorrosion of carbon steel in aqueous solutions[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,20012(2):1295-1307. |
| [24] | J. Jiang;M. M. Stack;A. Neville.Modelling the tribo-corrosion interaction in aqueous sliding conditions[J].Tribology International,200210(10):669-679. |
| [25] | S. Mischler.Triboelectrochemical techniques and interpretation methods in tribocorrosion: A comparative evaluation[J].Tribology International,20087(7):573-583. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%