The microstructure and mechanical properties of an as-cast Mg-4.0Sm-1.0Ca alloy were investigated during thermome-chanical treatments consisting of hot extrusion, rolling, and aging at 473 K. Mg41Sm5 phases containing Ca and needle-like Mg2Ca phases formed in the Mg matrix, and the average grain size and elongation were 4.2μm and 27%, respectively, after hot extrusion, which implied an increase in ductility. In addition, after the rolling, the grain size was further refined, and the tensile strength in-creased to 293 MPa. A new precipitate Mg3Sm was found in the peak-aged Mg-4.0Sm-1.0Ca alloy and this alloy displayed the best mechanical properties, with a peak hardness of 83 HV and ultimate tensile strength of 313 MPa; these properties were attributed to grain refinement strengthening, solid solution strengthening, work hardening, and precipitation strengthening.
参考文献
| [1] | A. A. Luo.Recent magnesium alloy development for elevated temperature applications[J].International Materials Reviews,20041(1):13-30. |
| [2] | Mohri T.;Saito N.;Nakamura M.;Mabuchi M..Microstructure and mechanical properties of a Mg-4Y-3RE alloy processed by thermo-mechanical treatment[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,19982(2):287-294. |
| [3] | T.J. Chen;W. Wang;D.H. Zhang;Y. Ma;Y. Hao.Development of a new magnesium alloy ZW21[J].Materials & design,2013Feb.(Feb.):555-565. |
| [4] | Ramirez A;Qian M;Davis B;Wilks T;StJohn DH.Potency of high-intensity ultrasonic treatment for grain refinement of magnesium alloys[J].Scripta materialia,20081(1):19-22. |
| [5] | J. F. Nie and B. C. Muddle.CHARACTERISATION OF STRENGTHENING PRECIPITATE PHASES IN A Mg-Y-Nd ALLOY[J].Acta materialia,20008(8):1691-1703. |
| [6] | Wang QD.;Zeng XQ.;Lu YZ.;Ding WJ.;Zhu YP.;Xu XP.;Mabuchi M.;Chen WD..Effects of Ca addition on the microstructure and mechanical properties of AZ91magnesium alloy[J].Journal of Materials Science,200112(12):3035-3040. |
| [7] | B. Kondori;R. Mahmudi.Effect of Ca additions on the microstructure, thermal stability and mechanical properties of a cast AM60 magnesium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20107/8(7/8):2014-2021. |
| [8] | Zhou, N.;Zhang, Z.;Dong, J.;Jin, L.;Ding, W..High ductility of a Mg-Y-Ca alloy via extrusion[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2013:103-110. |
| [9] | Du, Y. Z.;Qiao, X. G.;Zheng, M. Y.;Wu, K.;Xu, S. W..The microstructure, texture and mechanical properties of extruded Mg-5.3Zn-0.2Ca-0.5Ce (wt%) alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2015:164-171. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%