Sintered NdFeB magnets have complex microstructure that makes them susceptible to corrosion in active environments. The cur-rent paper evaluated the anticorrosion characteristics of multilayer titanium nitride ceramic coating applied through cathodic arc physical va-pour deposition (CAPVD) for protection of sintered NdFeB permanent magnets. The performance of ceramic coating was compared to the electrodeposited nickel coating having a copper interlayer. Electrochemical impedance spectroscopy (EIS) and cyclic polarization in simulated marine environment were employed to determine the rates of coatings degradation and passivation behaviour respectively. The coating mor-phologies and surface chemistry were studied with scanning electron microscope (SEM). X-ray diffraction (XRD) was used for identification of component phases in the coatings and the substrate. The results showed that the polarization resistance of ceramic coating increased with the exposure time. The rate of degradation of R_p for the ceramic coating had an extraordinary negative slope followed by a stable dmation, before declining towards the coating failure. In comparison the nickel coating with copper interlayer degraded sharply. The vapour deposited ceramic coating was found to have permeable defects that tended to "re-passivate" during exposure providing prolonged corrosion protection to the NdFeB substrate. The magnetic properties were unaffected and remained at par with the nickel coating having copper interlayer.
参考文献
| [1] | Hadjipanayis G C;Hazelton R C;Lawless K R .Cobalt-free permanent magnet materials based on iron-rare-earth alloys (invited)[J].Journal of Applied Physics,1984,55(06):2073. |
| [2] | Croat J J;Herbst J F;Lee R W;Pinkerton F E .Pr-Fe and Nd-Fe-based materials:A new class of high performance permanent magnets (invited)[J].Journal of Applied Physics,1984,35(06):2079. |
| [3] | Sagawa M;Fujimura S;Togawa N;Yamamoro H Matsura Y .New materials for permanent magnets based on Nd and Fe (Invited)[J].Journal of Applied Physics,1984,55(06):2083. |
| [4] | Mitchell P. .Corrosion protection of NdFeB magnets[J].IEEE Transactions on Magnetics,1990(5):1933-1935. |
| [5] | Szymura S;Bala H;Rabinovich Yu M;Sergeev V V Paw-lowska G .Structure,magnetic properties and corrosion be-haviour of sintered Nd16Fe76-xCrx8 magnets[J].Journal of Magnetism and Magnetic Materials,1991,94:113. |
| [6] | Williams C J;Narasimhan K S V L .Corrosion characteristics of RE-Fe-B permanent magnets[J].Journal of Applied Physics,1987,61:3766. |
| [7] | Mummert K;Aziz A M El;Barkleit G;Rodawald W Shultz L .Corrosion behaviour of NdFeB permanent magnets[J].Mater Corr,2000,51:13. |
| [8] | Gurappa I .Corrosion characteristics of permanent magnets in acidic environments[J].Journal of Alloys and Compounds,2003,360:236. |
| [9] | Sagawa M.;Tenaud P. .High coercivity Nd-Fe-B sintered magnet containing vanadium with new microstructure[J].IEEE Transactions on Magnetics,1990(5):1957-1959. |
| [10] | Rozendall E .Coercivity dependency of sintered NdFeB mag-nets on Al content and the alloying route[J].IEEE Transactions on Magnetics,1990,26:2631. |
| [11] | Tokuhara K;Hirosawa S .Corrosion resistance of NdFeB sin-tered magnets[J].Journal of Applied Physics,1991,69:5521. |
| [12] | Hirosawa S;Mino S;Tomizawa H .Improved corrosion resis-tance and magnetic properties of Nd-Fe-B type sintered mag-nets with Mo and Co[J].Journal of Applied Physics,1991,70:5844. |
| [13] | Yu Shengxue;Chen Ling .Preparation Technology and Performances of Zn-Cr Coating on Sintered NdFeB Permanent Magnet[J].Journal of Rare Earths,2006(2):223-226. |
| [14] | Tamborim S M;Azamboja D S;A M Sliba Silva;Costa I .Corrosion protection of NdFeB magnets by phosphating with tungsten incorporation[J].J Surf Coat Technol,2006,200:6826. |
| [15] | Zhang H;Song Y W;Song Z L .Electrodeposited nickel/alu-mina composite coating on NdFeB permanent magnets[J].J Mater Corr,2008,59:324. |
| [16] | Sagawa M;Hirosawa S;Tokunaga T;Yamamoto H Fujimura S Tsubukawa Y Shimizu R .Dependence of coercivity on the anisotropy field in the Nd_2Fe_(14)B type sintered magnets[J].Journal of Applied Physics,1987,61:3559. |
| [17] | Szymura S;Bala H;Pawlowska G;Rabinovich Yu M Sergeev V V Pokrovski D V J .Modification of the magnetic proper-ties and corrosion resistance of NdFeB permanent magnets with addition of cobalt[J].JOURNAL OF THE LESS-COMMON METALS,1991,175:185. |
| [18] | Femengel W;Rodewald W;Blank R;Schrey P Katter M Wall B .The influence of Co on the corrosion resistance of sin-ce tered Nd-Fe-B magnets[J].Journal of Magnetism and Magnetic Materials,1999,196:288. |
| [19] | A Ali;A Ahmad .Corrosion protection of sintered NdFeB magnets by CAPVD Ti_2N coating[J].J Mater Corr,2009,60(05):372. |
| [20] | Morita R.;Inoue S.;Miyano R.;Takikawa H.;Kobayashi A. Fujiwara E.;Uchida H.;Yatsuzuka M.;Azuma K. .Corrosion resistance of TiN coatings produced by various dry processes[J].Surface & Coatings Technology,2001(1/3):207-210. |
| [21] | Ahn S H;Lee J H;Kiln J G;Han J G .Localized corrosion mechanisms of the muitilayered coatings related to coating defects[J].Surf Coat Techol,2004,638:177. |
| [22] | Uchida H;Inoue S;Koterazawa K .Electrochemical evaluation of pin hole defects in TiN films prepared by rf reactive sput-tering [J].Mater Sci Eng A,1997,649:234. |
| [23] | Okamoto T;Fushima M;Takizawa K .[J].Corr Eng,1996,45:425. |
| [24] | Creus J.;Mazille H.;Sanchette F.;Jacquot P.;Idrissi H. .Improvement of the corrosion resistance of CrN coated steel by an interlayer[J].Surface & Coatings Technology,1998(2/3):183-190. |
| [25] | Liu C;Bi Q;Ziegele H;Leyland A Mattews A .Structure and corrosion properties of PVD Cr-N coatings[J].J Vac Sci Tecnol A,2002,20:772. |
| [26] | Yang, Q;Cai, F;Zhao, LR;Huang, X .Improving corrosion resistance of CrTiAlN coating by post-deposition treatments[J].Surface & Coatings Technology,2008(5/7):606-609. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%