The advanced temperature and stress test machine was introduced to determine the early cracking tendency of concrete with inclusion of light-burnt MgO under full restraint by tracking the development of thermal,physical and deformation properties.Results showed that light-burnt MgO being incorporated ranging between 4 wt％ and 6 wt％ of cementitious materials was beneficial to increase the maximum compressive stress and cracking stress of concrete by 0.37 MPa and 0.2 MPa on average respectively.The second zero stress temperature was reduced by 11.4 ℃ and the maximum temperature was slightly reduced while cracking thermal impact was significantly enhanced from 59.8 ℃ to 66.2 ℃.Sensitive anti-cracking coefficient F was forwarded to assess the early cracking tendency of concrete and the inclusion of 4 wt％ lightburnt MgO with activity of 109 s ranked the best in crack resistance.
参考文献
| [1] | R.Yang;C.D.Lawrence .Delayed ettringite formation in heat-cured Portland cement mortars[J].Cement and Concrete Research,1999(1):17-25. |
| [2] | BA Hengjing,SU Anshuang,GAO Xiaojian,TAO Qi.Cracking Tendency of Restrained Concrete at Early Ages[J].武汉理工大学学报（材料科学版）（英文版）,2008(02):263-267. |
| [3] | 李承木,杨元慧.氧化镁混凝土自生体积变形的长期观测结果[J].水利学报,1999(03):54-58. |
| [4] | 陈昌礼,FENG Lin-an,方坤河.氧化镁混凝土自生体积变形的反正切曲线模型[J].水力发电学报,2008(04):106-110. |
| [5] | 高培伟,吴胜兴,林萍华,吴中如,唐明述.氧化镁在不同养护条件下水化产物的形貌分析[J].无机化学学报,2007(06):1063-1068. |
| [6] | 陈波,蔡跃波,丁建彤.大坝混凝土抗裂性综合评价指标[J].混凝土,2008(10):5-7. |
| [7] | A. Bentur;K. Kovler .Evaluation of early age cracking characteristics in cementitious systems[J].Materials and structures,2003(257):183-190. |
| [8] | KANG Jingfu,JIANG Yongqi.Improvement of Cracking-resistance and Flexural Behavior of Cement-based Materials by Addition of Rubber, Particles[J].武汉理工大学学报（材料科学版）（英文版）,2008(04):579-583. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%