A new form of foam cement was produced by mixing alkali-activated slag,clay,a small amount of polypropylene fibers with prepared foam during stirring.The preparation of the material is quite different from the normal one,which is produced just at room temperature and without baking.The fabrication of this energy-saving and low-price material can be favorable for lowering carbon emission by using recycled industrial wastes.Thermal conductivity of 0.116 W/(m·k),compressive strength of 3.30 MPa,flexural strength of 0.8 MPa and density of 453 kg/m3 can be achieved after 28 days aging.The hydration product is C-S-H with less Ca(OH)2,calcium aluminum and zeolite,which was characterized by X-ray diffraction(XRD) measurement.This prospective foam cement may be expected to be an excellent economical energy-saving building material.
参考文献
| [1] | F.K. Akthar;J.R.G. Evans .High porosity (>90percent) cementitious foams[J].Cement and Concrete Research,2010(2):352-358. |
| [2] | Li GQ;Muthyala VD .A cement based syntactic foam[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):77-86. |
| [3] | Chaosheng Tang;Bin Shi;Wei Gao;Fengjun Chen;Yi Cai .Strength and mechanical behavior of short polypropylene fiber reinforced and cement stabilized clayey soil[J].Geotextiles and geomembranes,2007(3):194-202. |
| [4] | F. Puertas;T. Amat;A. Fernandez-Jimenez .Mechanical and durable behaviour of alkaline cement mortars reinforced with polypropylene fibres[J].Cement and Concrete Research,2003(12):2031-2036. |
| [5] | A. Just;B. Middendorf .Microstructure of high-strength foam concrete[J].Materials Characterization,2009(7):741-748. |
| [6] | E.K. Kunhanandan Nambiar;K. Ramamurthy .Influence of filler type on the properties of foam concrete[J].Cement & concrete composites,2006(5):475-480. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%