Failure Behavior of Thermal Barrier Coatings on Cylindrical Superalloy Tube Under Thermomechanical Fatigue

金属学报(英文版), 2013, 26(4): 404-408. doi: 10.1007/s40195-013-0028-9

^1, , ^2, , ^3,

1.Shenyang Aeroengine Research Institute, Aviation Industry Corporation of China, Shenyang 110015, China;Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences,Shenyang 110016, China

2.Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences,Shenyang 110016, China

3.Department of Intelligent Mechanical Engineering, Fukuoka Institute of Technology, Higashi-ku, Fukuoka, 811-0295,Japan

Failure Behavior of Thermal Barrier Coatings on Cylindrical Superalloy Tube Under Thermomechanical Fatigue

Zhubing CHEN ^1, , Zhongguang WANG ^2, , Shijie ZHU ^3,

1.Shenyang Aeroengine Research Institute, Aviation Industry Corporation of China, Shenyang 110015, China;Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences,Shenyang 110016, China

2.Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences,Shenyang 110016, China

3.Department of Intelligent Mechanical Engineering, Fukuoka Institute of Technology, Higashi-ku, Fukuoka, 811-0295,Japan

Keywords： Thermal barrier coating

参考文献

[1]	A. G. Evans;D. R. Mumm;J. W. Hutchinson;G. H. Meier;F. S. Pettit .Mechanisms controlling the durability of thermal barrier coatings[J].Progress in materials science,2001(5):505-553.
[2]	Z.W. Huang;Z.G. Wang;S.J. Zhu;F.H. Yuan;F.G. Wang .Thermomechanical fatigue behavior and life prediction of a cast nickel-based superalloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):308-316.
[3]	B. Baufeld;E. Tzimas;P. Hahner .Phase-angle effects on damage mechanisms of thermal barrier coatings under thermomechanical fatigue[J].Scripta materialia,2001(7):859-865.
[4]	E.TZIMAS;H.MULLEJANS .FAILURE OF THERMAL BARRIER COATING SYSTEMS UNDER CYCLIC THERMOMECHANICAL LOADING[J].Acta materialia,2000(18/19):4699-4707.
[5]	F.H. Yuan;Z.X. Chen;Z.W. Huang;Z.G. Wang;S.J. Zhu .Oxidation behavior of thermal barrier coatings with HVOF and detonation-sprayed NiCrAlY bondcoats[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(6):1608-1617.
[6]	B. Baufeld;M. Bartsch;P. Broz .Microstructural changes as postmortem temperature indicator in Ni-Co-Cr-Al-Y oxidation protection coatings[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):162-171.

上一张下一张

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%