Effects of Carbon Content and Microstructure on Corrosion Property of New Developed Steels in Acidic Salt Solutions

金属学报(英文版), 2014, 27(1): 115-123. doi: 10.1007/s40195-013-0007-1

^1, , ^2, , ^3,

1.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

2.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China;Key Laboratory of Corrosion and Protection(Ministry of Education), Beijing 100083, China

3.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China;Key Laboratory of Corrosion and Protection(Ministry of Education), Beijing 100083, China

基金项目: Fundamental Research Funds for the Central Universities(FRF-TP-12-144A) The authors acknowledge the financial support from the National Natural Science Foundation of China(.51171025 and 51271023) the National Network of Field Observation & Scientific Research on Material Environmental Corrosion

Effects of Carbon Content and Microstructure on Corrosion Property of New Developed Steels in Acidic Salt Solutions

Feilong Sun ^1, , Xiaogang Li ^2, , Xuequn Cheng ^3,

1.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China

2.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China;Key Laboratory of Corrosion and Protection(Ministry of Education), Beijing 100083, China

3.Corrosion and Protection Center, University of Science and Technology Beijing, Beijing 100083, China;Key Laboratory of Corrosion and Protection(Ministry of Education), Beijing 100083, China

Keywords： Carbon content

参考文献

[1]	Y.-S. Choi;J.-J. Shim;J.-G. Kim .Corrosion behavior of low alloy steels containing Cr, Co and W in synthetic potable water[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):148-156.
[2]	Y.-S. Choi;J.-J. Shim;J.-G. Kim .Effects of Cr, Cu, Ni and Ca on the corrosion behavior of low carbon steel in synthetic tap water[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2005(1/2):162-169.
[3]	M. Murayama;Murayama;T. Nishimura;Nishimura;K. Tsuzaki;Tsuzaki .Nano-scale Chemical Analysis Of Rust On A 2% Si-bearing Low Alloy Steel Exposed In A Coastal Environment[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(8):2159-2165.
[4]	D. CLOVER;B. KINSELLA;B. PEJCIC .The influence of microstructure on the corrosion rate of various carbon steels[J].Journal of Applied Electrochemistry,2005(2):139-149.
[5]	Z.F. Wang;P.H. Li;Y. Guan;Q.F. Chen;S.K. Pu .The corrosion resistance of ultra-low carbon bainitic steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(5):954-961.
[6]	J.B. Sun;G.A. Zhang;W. Liu;M.X. Lu .The formation mechanism of corrosion scale and electrochemical characteristic of low alloy steel in carbon dioxide-saturated solution[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2012(Apr.):131-138.
[7]	S.H. Wang;C.C. Chiang;S.L.I. Chan .Effect of initial microstructure on the creep behavior of TMCP EH36 and SM490C steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):288-295.

上一张下一张

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%