Defects seriously influence the optical properties and mechanical properties of CVDZnS.The deposition technique was introduced and experiment methods such as SEM,TEM and OM were adopted to study the defects:hexagonal phase,abnormally large grains,micro-cracks,micro-pores and impurities.The microstructures of these defects were observed,and the formation mechanisms of these defects were analyzed.Hexagonal ZnS as an impurity causes anisotropy in different directions with different refraction indexes and increases the scattering of CVDZnS.Increasing the deposition temperature can inhibit the formation of the hexagonal phase.The main reason for the growth of abnormally large grains in CVDZnS is high deposition rate.The lower deposition temperature increases growth stress in CVDZnS,which consequently results in the bowing of CVDZnS plates,and introduces microscopic defects such as grain blending and micro-cracks in the crystal.Micro-pores and impurities are induced by high reactant concentration in the local deposition chamber,which can be avoided by improving the gas flowing so as to make the concentration more uniform.
参考文献
| [1] | Harris D.Infrared Windows and Dome Material[M].San Diego Academic Press,San Diego,1999:4-19. |
| [2] | 范金荣.精确制导武器信息化关键技术分析[J].现代防御技术,2003(04):27-30. |
| [3] | Harris D C;Parsons W F;Pappis J et al.Development of hot-pressed and chemical-vapor-deposited zinc sulfide and zinc selenide in United States for optical windows[J].Proceedings of the SPIEInt Soc Opt Eng,2007,6545:ArtNo654502. |
| [4] | McCloy J .International development of chemical vapor deposited zinc sulfide[J].Proceedings of Spie-the International Society for Optical Engineering,2007,6545:ArtNo654503. |
| [5] | McCloy J S;Korenstein R;Zelinski B .Effect of temperature,pressure,and metal promoter on the recrystallized structure and optical transmission of chemical vapor deposition zinc sulfide[J].Journal of the American Ceramic Society,2009,92(08):1725. |
| [6] | Wiedemeier H .Thermodynamic estimations of defect equilibria and vacancy concentrations in ZnS[J].Zeitschrift fur Anorganische und Allgemeine Chemie,2006(10/11):1717-1727. |
| [7] | Structural Defects in CVD ZnS[J].Inorganic materials,2010(1):6. |
| [8] | McCloy J;Korenstein R .The Effect of metal on the formation of multispectral zinc sulfide[J].Proceedings of Spie-the International Society for Optical Engineering,2009,7302:ArtNo73020N. |
| [9] | McCloy J;Korenstein R .Variability in chemical vapor deposited zinc sulfide:Assessment of legacy and international CVD ZnS materials[J].Proceedings of Spie-the International Society for Optical Engineering,2009,7302:ArtNo73020M. |
| [10] | 霍承松,杨海,付利刚,石红春,鲁泥藕,赵永田,魏乃光,孙加滢,余怀之,苏小平.大口径多光谱ZnS头罩的研制[J].红外与激光工程,2008(04):719-722. |
| [11] | E. V. Yashina;E. M. Gavrishchuk;V. B. Ikonnikov .Mechanisms of Polycrystalline CVD ZnS Densification during Hot Isostatic Pressing[J].Inorganic materials,2004(9):901-904. |
| [12] | Shchttrov A F;Gsbtidhvhuk E M;Ikonnikov V B et al.Effect of hot isostatic pressing on the elastic and optical properties of polycrystalline CVDZnS[J].Inorganic Materials,2004,40(04):336. |
| [13] | Pickering M A;Taylor R L .Gradient infrared optical material prepared by chemical vapour deposition process[J].Applied Optics,1986,25(19):3364. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%