The physical and mechanical properties of metal matrix composites were improved by the addition of reinforcements.The mechanical prop-erties of particulate-reinforced metal-matrix composites based on aluminium alloys(6061 and 7015)at high temperatures were studied.Tita-nium diboride(TiB2)particles were used as the reinforcement.All the composites were produced by hot extrusion.The tensile properties and fracture characteristics of these materials were investigated at room temperature and at high temperatures to detemvne their ultimate strength and strain to failure.The fracture surface was analysed by scanning electron microscopy.TiB2 particles provide high stability of the alumin-ium alloys(6061 and 7015)in the fabrication process.An improvement in the mechanical behaviour was achieved by adding TiB2 particles as reinforcement in both the aluminium alloys.Adding TiB2 particles reduces the ductility of the aluminium alloys but does not change the microscopic mode of failure,and the fracture surface exhibits a ductile appearance with dimples formed by coalescence.
参考文献
[1] | Ghosh A.K.Fundamentals of Metal-Matrix Composites[M].Butterworth,London,1993:43. |
[2] | Prabu S.B;Kantnamoorthy L .Microstructure-based finite element analysis of failure prediction in particle-rein-forced metal-matrix-composite[J].Journal of Materials Processing Technology,2008,207(1-3):53. |
[3] | PENG Jihua,LI Wenfang,HUANG Fangliang,TIAN Jun,LIU Gang,DU Jun.Microstructure evolution of rare earth Pr modified alumina-silicate short fiber-reinforced Al-Si metal matrix composites[J].稀有金属(英文版),2009(02):164-168. |
[4] | DENG Chunfeng,ZHANG Xuexi,MA Yanxia,WANG Dezun.Fabrication of aluminum matrix composite reinforced with carbon nanotubes[J].稀有金属(英文版),2007(05):450-455. |
[5] | Hunt W.H.Diswntinuously-reinforced aluminum:the second generation,[in]Processing and Fabrication of Advanced Materials Ⅲ[M].TMS:Warrendale:PA,1994:663. |
[6] | Munro R.G .Material properties of titanium diboride[J].Journal of Research of the National Institute of Standards and Technology,2000,105:709. |
[7] | Kumar S;Chakraborty M;Sarma V.S;Murty B.S .Ten-site and wear behaviour of in situ Al-7Si/TiB2 particulate composites[J].WEAR,2008,265:134. |
[8] | Lloyd D.J .Particle reinforced Al and Mg matrix composites[J].International Materials Reviews,1994,39(01):1. |
[9] | Del Rio E;Nash J.M;Williams J.C;Breslin M.C, Daehn G.S .Co-continuous wmposites for high-temperature applications[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2007,463:115. |
[10] | Smagorinski ME.;Grenier S.;Brzezinski T.;Kim G.;Tsantrizos PG. .The properties and microstructure of Al-based composites reinforced with ceramic particles[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1):86-90. |
[11] | Arsenault R.J;Fishman S;Taya M .Deformation and fracture behavior of metal-ceramic matrix composite materi-als[J].Progress in Materials Science,1994,38(01):1. |
[12] | Ernst F .Metal-oxide interfaces[J].Materials Science and Engineering,1995,14(03):97. |
[13] | Hatano T .Dynamics of a dislocation bypassing an impenetrable precipitate: The Hirsch mechanism revisited[J].Physical review, B. Condensed matter and materials physics,2006(2):102-1-102-4-0. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%