The hot deformation behavior of IN690 superalloy was characterized in a temperature range of 1273-1473 K and a strain rate range of 0.01-10 s-1 using uniaxial compression tests on process annealed material. The constitutive relations between flow stress and effective strain,effective strain rate as well as deformation temperature were studied. It can be concluded that the flow stress significantly reduces with the deformation temperature of IN690 superalloy increasing. Whereas, there is a significant increase of flow stress when the strain rate increases from 0.1 s-1 to 10 s-1. Based on the hyperbolic-sine Arrhenius-type equation, a constitutive equation considering compensation of strain was developed. The activation energy and the material constants (Q, n and in A) decrease as the deformation strain increases. The strain dependent term is successfully incorporated in the constitutive equation through a quartic equation. A good agreement between the experimental data and the predicted results has been achieved, indicating that the proposed constitutive equation and the methods of determing the material constants are suitable to model the high temperature deformation behavior of IN690 superalloy.
参考文献
| [1] | Gonzalez-Rodriguez J.G;Casales M;Espinoza-Medina M.A;Angeles-Chavez C,Izquierdo G,and Guardian R .Microstructural evolution of alloy 690 during sensitization at 700℃[J].Materials Characterization,2003,51(05):309. |
| [2] | Kim H.P;Hwang S.S;Lim Y.S;Kuk,I.H,Kim J.S .Effect of heat treatment and chemical composition on caustic stress corrosion cracking of Alloy 600 and Alloy 690[J].Key Engineering Materials,2000,183-187:707. |
| [3] | B.T. Lu;J.L. Luo;B. Peng .Condition for Lead-Induced Corrosion of Alloy 690 in an Alkaline Steam Generator Crevice Solution[J].Corrosion: The Journal of Science and Engineering,2009(9):601-610. |
| [4] | Lumsden J;cilree A.Factors affecting PBSCC in alloy 600 and alloy 690 steam generator tubing[A].Whistler,2007:1990. |
| [5] | Dwivedi S.N;Balakrishnan R.Development of constitutive equations and processing maps for Inconel 718[A].Dallas,1990:99. |
| [6] | Dwivedi S.N;Balakrishnan R.Development of constitutive equations and processing maps for Al 2024[A].Dallas,1990:303. |
| [7] | Pu ZJ.;Zou D.;Wu KH. .DEVELOPMENT OF CONSTITUTIVE RELATIONSHIPS FOR THE HOT DEFORMATION OF BORON MICROALLOYING TIAL-CR-V ALLOYS[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(0):780-787. |
| [8] | Rao K.P;Hawbolt E.B .Development of constitutive relationships using compression testing of a medium carbon steel[J].Journal of Engineering Materials and Technology,Transactions of the ASME,1992,114(01):116. |
| [9] | Cabrera E.S.P .A Constitutive description of aluminum-l% magnesium alloy deformed under hot-working conditions[J].Journal of Engineering Materials and Technology,Transactions of the ASME,2001,123(03):301. |
| [10] | D. Liu,Y.H. Yang,J. Geng,Z.J. Luo.CONSTITUTIVE RELATIONSHIP OF IN718 ALLOY FOR THERMOVISCOPLASTIC AND MICROSTRUCTURE EVOLUTION COUPLED ANALYSIS[J].金属学报（英文版）,2007(05):373-379. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%