A Y2O3 dispersion strengthened nickel-based superalloy sheet (0.15 mm thick) was prepared by electron beam physical vapor deposition (EB-PVD) technology. Different heat treatments were used to improve the mechanical properties of the alloy sheet. Differential thermal analysis (DTA) was used to examine the thermal stability of the as-deposited sheet. Element contents, phase composition and microstructure investigations on as-deposited and heat treated specimens were performed by X-ray fluorescence spectrometer (XRF), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Tensile tests were conducted at room temperature on specimens as-deposited and heat treated. The results show that the as-deposited sheet is composed of equiaxed grains on the substrate side and columnar grains on the evaporation side. The as-deposited sheet shows poor ductility due to micropores between columnar grains. The strength and ductility can be improved effectively by annealing at 800℃ for 3 h. For samples treated at 1100℃, the strength drops down due to the precipitates of Y3Al5O12(YAG).
参考文献
| [1] | Movchan B.A .EB-PVD technology in the gas turbine industry:present and future[J].JOM-Journal of the Minerals Metals and Materials Society,1996,48(11):40. |
| [2] | Vennemann A;Langmaack E;Nembach E .On the temperature dependence of the critical resolved shear stress of the γ'-strengthened superalloy NIMONIC PE16[J].Scripta Materialia,2002,46(10):723. |
| [3] | Miller M.K;Babu S.S;Vitek J.M .Stability of γ' precipitates in a PWA1480 alloy[J].Intermetallics,2007,15(5-6):757. |
| [4] | Mukhopadhyay D.K;Froes F.H;Gelles D.S .Development of oxide dispersion strengthened ferritic steels for fusion[J].Journal of Nuclear Materials,1998,258-263:1209. |
| [5] | Cook BA.;Han SH.;Vining CB.;Harringa JL. .SI80GE20 THERMOELECTRIC ALLOYS PREPARED WITH GAP ADDITIONS[J].Journal of Applied Physics,1995(9):5474-5480. |
| [6] | Kuwabara T;Kurishita H;Hasegawa M .Development of an ultra-fine grained V-1.7mass% Y alloy dispersed with yttrium compounds having superior ductility and high strength[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2006,417(1-2):16. |
| [7] | Mujahid M;Martin J.W .Development ofmicrostructures of high grain aspect ratio during zone annealing of oxide dispersion strengthened superalloys[J].Materials Science and Technology,1994,10(08):703. |
| [8] | Movchan BA.;Lemkey FD. .Some approaches to producing microporous materials and coatings by EB PVD[J].Surface & Coatings Technology,2003(1):90-100. |
| [9] | B.A.Movchan .Inorganic materials and coatings produced by EBPVD[J].Surface Engineering,2006(1):35-46. |
| [10] | He X.D;Xin Y;Li M.W;Sun Y .Microstructure and mechanical properties of ODS Ni-based superalloy foil produced by EB-PVD[J].Journal of Alloys and Compounds,2009,467(1-2):347. |
| [11] | Effects Of Substrate Rotation On The Microstructure Of Metal Sheet Fabricated By Electron Beam Physical Vapor Deposition[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2009(11):5831-5836. |
| [12] | Iino Y .Effects of high temperature air and vacuum exposure on tensile properties and fracture of ODS alloy MA6000[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1997,234-236:802. |
| [13] | Schulz U;Fritscher K;Peters M .EB-PVD Y2O3-and CeO2/Y2O3-stabilized zirconia thermal barrier coatings -Crystal habit and phase composition[J].Surface and Coatings Technology,1996,82:259. |
| [14] | Li X.H .Research on Large Scale Ni-based Superalloy Sheets Deposited by EB-PVD[D].哈尔滨工业大学学报,2006. |
| [15] | GONG Feng,GUO Bin,ZHOU Jian,SHAN Debin.Size effects on flow stress of C3602 in cylinder compression with different lubricants[J].稀有金属（英文版）,2009(05):528-532. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%