Ti(C,N)-based cermets were coated with TiAlN using multi-arc ion plating technology. Sliding wear tests were performed on the coated cermets. The microstructure and morphologies oftbe coated cermets before and after friction and wear tests were characterized. The results show that the TiAlN coating surface was smooth and its root mean square roughness was 16.6 nm. The hardness (HK) of TiAlN coating lay-ers reached approximately 3200 and the critical load (Lc) under which the coating failure occurred was 59 N. The sliding wear test results show that the friction coefficients of the TiAlN-coated cermets were lower than that of the cermets without any coating. Under the same load, the adhesion phenomenon of the counterpart materials on the specimens was improved and the mean friction coefficient increased with in-average friction coefficient of the TiAlN-coated cermets was lower under a higher load. The wear mechanisms of the TiAIN-coated cermets were mainly adhesive and abrasive wear.
参考文献
| [1] | Nouari M;List G;Girot F;Coupard D .Experimental analysis and optimisation of tool wear in dry machining of aluminium alloys[J].Wear,2003,255(7-12):1359. |
| [2] | ZHENG Liyun,XIONG Weihao,YAN Xianmei,LI Guo'an.Microstructure and mechanical properties of hot isostatically pressed cermets with TiN coatings[J].稀有金属(英文版),2006(06):643-648. |
| [3] | Andersen K N;Bienk E J;Schweitz K O;Reitz H,Chevallier J,Kringhoj P,Bottiger J .Deposition,microstructure and mechanical and tribological properties of magnetron sputtered TiN/TiAlN multilayers[J].Surface and Coatings Technology,2000,123(2-3):219. |
| [4] | Harris S G;Doyle E D;Vlasveld A C;Audy J,Quick D .A study of the wear mechanisms of Ti1-x-AlxN and Ti1-x-yAlxCryN coated high-speed steel twist drills under dry machining conditions[J].Wear,2003,254(7-8):723. |
| [5] | Yoon S Y;Kim J K;Kim K H .A comparative study on tribological behavior of TiN and TiAlN coatings prepared by arc ion plating technique[J].Surface and Coatings Technology,2002,161(2-3):237. |
| [6] | Wang D Y;Chang C L;Wong K W;Li Y W,Ho W Y .Improvement of the interracial integrity of (Ti,Al)N hard coatings deposited on high speed steel cutting tools[J].Surface and Coatings Technology,1999,120-121:388. |
| [7] | Donohue L A;Smith I J;Munz W D;Petrov I,Greene J E .Microstructure and oxidation-resistance of Ti1-x-y-zAlxCryYzN layers grown by combined steered-arc/ unbalanced-magnetron-sputter deposition[J].Surface and Coatings Technology,1997,94-95:226. |
| [8] | Mayrhofer PH.;Hovsepian PE.;Mitterer C.;Munz WD. .Calorimetric evidence for frictional self-adaptation of TiAlN/VN superlattice coatings[J].Surface & Coatings Technology,2004(0):341-347. |
| [9] | Huang Z P;Sun Y;Bell T .Friction behaviour of TiN,CrN and (TiAI)N coatings[J].Wear,1994,173(1-2):13. |
| [10] | 刘英才,李静,尹衍升.Fe3Al-Cu基刹车材料的制备及其摩擦学特性[J].中国有色金属学报,2005(02):192-197. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%