AerMet100 ultra-high strength steel plates with a thickness of 2 mm were welded using a CO2 laser welding system. The inlfuences of the welding process parameters on the morphology and microstructure of the welding joints were investigated, and the mechanical property of the welding joints was analyzed. The experimental results showed that the fusion zone of welding joint mainly consisted of columnar grains and a ifne dendrite substructure grew epitaxially from the matrix. With the other conditions remaining unchanged, a finer weld microstructure was along with the scanning speed increase. The solidification microstructure gradually transformed from cellular crystal into dendrite crystal and the spaces of dendrite secondary arms rose from the fusion line to the center of the fusion zone. In the fusion zone of the weld, the rapid cooling caused the formation of martensite, which led the microhardness of the fusion zone higher than that of the matrix and the heat affected zone. The tensile strength of the welding joints was tested as 1 700 MPa, which was about 87% of the matrix. However, the tensile strength of the welding joints without defects existed was tested as 1832 MPa, which was about 94% of the matrix.
参考文献
| [1] | Little CD;Machmeier PM .High Strength Fracture Resistant Weldable Steels[P].US Patent:4076525,1978. |
| [2] | Dahl J .AerMet 100-An Advanced Steel for the Aerospace Industry[J].Adv Mater Tech Inter,1991,2(03):40-45. |
| [3] | Thomas J;Caffrey Mc .Combined Strength and Toughness Characterize New Aircraft Alloy[J].Advanced Materials and Processes,1992,2(03):47-53. |
| [4] | Wang R .AerMet100 Ultrahigh Strength Steel with the Unique Combination of Properties[J].J Beijing Univ Aeronaut Astronaut,1996,22(06):639-644. |
| [5] | Guan ZZ.Laser Processing Technology Handbook[M].北京:中国计量出版社,1998 |
| [6] | Raghavan A;Machmeier PM .Transmission Electron Microscopy Examination of Hardening and Toughening Phenomena in AerMet 100[J].Metallurgical and Materials Transactions,1993,24A:1943-1955. |
| [7] | Sato K .Improving the Toughness of Ultrahigh Strength Steel[D].Berkeley,California:University of California,2002. |
| [8] | Liang JK .Reifnement of Grain and Enhancement of Reverted Austenite Stability for AerMet100 Steel[D].Xi'an:Northwestern Polytechnical University,2009. |
| [9] | Wang C .Study of Laser Welding of 400MPa Super Steel and Its Weldability[D].Beijing:University of Tsinghua University,2002. |
| [10] | Lee S;Kim BC;Kwon D .Correlation of Microstructure and Fracture Properties in Weld Heat-affected Zones of Thermomechanically Controlled Processed Steels[J].Metallurgical and Materials Transactions,1992,23A(10):2803-2816. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%