The phosphated and cerium nitrate post-sealed galvanized steel was ifrstly scratched to expose zinc layer and then placed in neutral salt spray (NSS) chamber for different durations. The microstructure and compositions of the scratches were investigated using SEM and EDS. The phases of the corrosion products were examined through XRD. The self-healing mechanism of the composite coatings was discussed. The experimental results show that the composite coatings have an excellent corrosion resistance. The corrosion products increase with corrosion time and ifnally cover the whole scratch. They contain phosphorous, cerium, oxygen, chloride and zinc, and are ifne needle and exceedingly compact. The composite coatings are favorable self-healing. During corrosion, the self-healing ions such as Ce3+, Ce4+, PO43-, Zn2+ in the composite coatings were dissolved, migrated, recombined, and covered the exposed zinc, impeding zinc corrosion. The self-healing process of the scratches on the composite coatings can be divided into three stages, about 2 h, 4 h, and 24 h, respectively.
参考文献
| [1] | Dech OS;Thaiwatthana S;Chairaungsri T .Post-Treatment by Sodium Silicate after Zinc Phosphating on Cold-Rolled Steel[J].Chiang Mai Journal of Science,2012,39:30-40. |
| [2] | Daimon K Heller;William G. Fahrenholtz;Matthew J. O'Keefe .Effect of Phosphate Source on Post-Treatment of Cerium-Based Conversion Coatings on Al 2024-T3[J].Journal of the Electrochemical Society,2009(11):C400-C406. |
| [3] | Tang N.;Gorecki G.;Vanooij WJ. .COMPARATIVE EIS STUDY OF PRETREATMENT PERFORMANCE IN COATED METALS [Review][J].Progress in Organic Coatings: An International Review Journal,1997(4):255-263. |
| [4] | Lindert A;Maurer JI;Kent G .Chromate-Free Post-Treatments[J].Products Finishing,1986,50:48-53. |
| [5] | Claffey WJ;Reid AJ .Post Treatment of Phosphated Metal Surfaces by Organic Titanates[P].US Patent 4 656 097 |
| [6] | Susac D;Leung CW;Sun X et al.Comparison of a Chromic Acid and a BTSE Final Rinse Applied to Phosphated 2024-T3 Aluminum Alloy[J].Surface and Coatings Technology,2004,187:216-224. |
| [7] | You W;Lu JT;Lin BL .Corrosion Resistance of Phosphating/Silane Composite Film on Hot-Dip Galvanized Steel Sheet (in Chinese)[J].Materials Protection,2008,41:34-36. |
| [8] | Bi-Lan Lin;Jin-Tang Lu;Gang Kong .Effect of molybdate post-sealing on the corrosion resistance of zinc phosphate coatings on hot-dip galvanized steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(4):962-967. |
| [9] | Lin BL;Lu JT;Kong Gang .Synergistic Corrosion Protection for Galvanized Steel by Phosphating and Sodium Silicate Post-Sealing[J].Surface and Coatings Technology,2008,202:1831-1838. |
| [10] | Lin BL;Lu JT;Kong G .Composition and Performance of the Com-posite Coatings Obtained by Phosphating and Cerium Nitrate Post-Sealing on Galvanized Steel[J].Journal of Rare Earths,2007,25:S461-S463. |
| [11] | Kendig M;Jeanjaquet S;Addison R et al.Role of Hexavalent Chromium in the Inhibition of Corrosion of Aluminum Alloys[J].Surface and Coatings Technology,2001,140:58-63. |
| [12] | Nosonovsky M;Bhushan B .Surface Self-Organization:From Wear to Self-Healing in Biological and Technical Surfaces[J].Applied Surface Sinence,2010,256:3982-3986. |
| [13] | Yuan MR;Lu JT;Kong G et al.Self Healing Ability of Silicate Conversion Coatings on Hot Dip Galvanized Steels[J].Surface and Coatings Technology,2011,205:4507-4513. |
| [14] | Zheludkevich ML;Tedim J;Freire CSR .Self-Healing Protective Coatings with "Green” Chitosan Based Pre-Layer Reservoir of Corrosion Inhibitor[J].Journal of Materials Chemistry,2011,21:4805-4812. |
| [15] | Montemor MF;Snihirova DV;Taryba M G et al.Evaluation of Self-Healing Ability in Protective Coatings Modiifed with Combinations of Layered Double Hydroxides and Cerium Molybdate Nanocontainers Filled with Corrosion Inhibitors[J].Electrochimica Acta,2012,60:31-40. |
| [16] | Samadzadeh, M;Boura, SH;Peikari, M;Kasiriha, SM;Ashrafi, A .A review on self-healing coatings based on micro/nanocapsules[J].Progress in Organic Coatings: An International Review Journal,2010(3):159-164. |
| [17] | González GY;MolJ MC;Muselle T et al.SECM Study of Defect Repair in Self-Healing Polymer Coatings on Metals[J].Electrochem Communications,2011,13:169-173. |
| [18] | Yabuki A;Okuno H .Self-Healing Corrosion Protective Capability of Polymer Coatings for Aluminum[J].J Japan Institute of Light Metals,2011,61:724-728. |
| [19] | Hamdy AS;Butt DP .Novel Smart Stannate Based Coatings of Self-healing Functionality for AZ91D Magnesium Alloy[J].Electrochimica Acta,2013,97:296-303. |
| [20] | Aramaki K .XPS and EPMA Studies on Self-healing Mechanism of a Protective Film Composed of Hydrated Cerium(III)Oxide and Sodium Phosphate on Zinc[J].Corrosion Science,2003,45:199-210. |
| [21] | Lin BL;Lu JT .Self-Healing Mechanism of the Composite Coatings Obtained by Phosphating and Silicate Sol Post-Sealing[J].Transactions of Nonferrous Metals Society of China,2014,24:2723-2728. |
| [22] | S. Jegannathan;T. S. N. Sankara Narayanan;K. Ravichandran;S. Rajeswari .Performance of zinc phosphate coatings obtained by cathodic electrochemical treatment in accelerated corrosion tests[J].Electrochimica Acta,2005(2):247-256. |
| [23] | Lin BL;Lu JT;Li YC .Growth Mechanism of Composite Coatings Obtained by Phosphating and Cerium Nitrate Post-sealing on Galvanized Steel[J].Chinese J Nonferrous Met,2014,24:1008-1013. |
| [24] | Ride D.CRC Handbook of Chemistry and Physics (in Chinese)[M].Boca Raton:CRC Press,1999:8-11. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%