RE13Fe84Cr3(RE=Ce, Pr, Tb, Er) and Pr13-xFe84Cr3Tix(x=0, 2, 4, 6) alloy powders were prepared by arc smelting method and high energy ball milling technique. The phase structure and the morphology of the alloy powders were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM), and their microwave absorbing properties were determined by a vector network analyzer. The results show that the alloys with light rare earths (Ce, Pr) have good low frequency absorbing property and those with heavy rare earths (Tb, Er) exhibit an improved high frequency absorbing property. The minimum refl ectivity at the absorbing peak frequency of RE13Fe84Cr3(RE=Ce, Pr, Tb, Er) are -9.49 dB at 5.76 GHz , -22.38 dB at 7.92 GHz , -18.52 dB at 11.68 GHz and -17.59 dB at 10.24 GHz, respectively. The absorbing bandwidth under -10 dB of the Pr13Fe84Cr3 powder was widened from 1.91 GHz to 3.89 GHz by adding 2% Ti, but the refl ectivity of the alloy was increased from -22.38 dB to -14.91 dB.
参考文献
| [1] | 王毅,徐辉,麻桂荣,郭幼英.城市电磁环境的新问题[J].城市管理与科技,2001(03):14-18. |
| [2] | Thoumire O.;Teillet J.;Beucher E.;Atmani H. .Structural, mechanical and magnetic properties of nitrided FeSi and FeSiAl sheets[J].Journal of Magnetism and Magnetic Materials,1999(0):346-348. |
| [3] | Kim, MS;Min, EH;Koh, JG .Comparison of the effects of particle shape on thin FeSiCr electromagnetic wave absorber[J].Journal of Magnetism and Magnetic Materials,2009(6):581-585. |
| [4] | V.M. Petrov;V.V. Gagulin .Microwave Absorbing Materials[J].Inorganic Materials,2001(2):93-98. |
| [5] | T.D.Zhou;D.F.Liang;L.J.Deng;D.C.Luan .Electron Structure and Microwave Absorbing Ability of Flaky FeSiAl Powders[J].Journal of materials science & technology,2011(2):170-174. |
| [6] | Katsu Yanagimoto;Kazuhiko Majima;Satoshi Sunada .Effect of Powder Compositions on GHz Microwave Absorption of EM Absorbing Sheets[J].粉体ぉょび粉末冶金,2004(4):293-296. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%