The effect of fly ash and silica fume on hydration rate and strength of cement in the early stage was studied. Contrast test was applied to the complex cementitious system to investigate the hydration rate. Combined with mechanical strength, the influence of fly ash and silica fume during the hydration process of complex binder was researched. The peak of the rate of hydration heat evolution and the mechanical strength decreased as the ratio of fly ash increased, however, as the ratio of silica fume increased, the peak of the rate of hydration heat evolution and the mechanical strength increased obviously. When the ratios of fly ash and silica fume are 10%and 5%, the peak of the rate of hydration heat evolution is the highest. At the same time 7 days of flexural and compressive strength are the highest as 8.89 MPa and 46.52 MPa, respectively. Fly ash and silica fume are the main factors affecting the hydration rate and the mechanical property.
参考文献
| [1] | 刘军,刘润清,刘智,李莉,吴江.低温混凝土抗冻临界强度影响因素的研究[J].沈阳建筑大学学报（自然科学版）,2005(03):228-231. |
| [2] | 刘军,李振国,田悦,刘润清.低温条件下矿物掺合料对混凝土强度发展及抗冻临界强度的影响[J].沈阳建筑大学学报（自然科学版）,2006(03):415-418,427. |
| [3] | 吕林女,何永佳,丁庆军,胡曙光.多组分水泥基材料的水化放热行为[J].水泥,2004(09):1-3. |
| [4] | 唐明,刘宏亮,李婧琦.同水胶比下混凝土中水泥-矿渣-粉煤灰-硅灰的混料效应[J].混凝土,2011(12):1-4,15. |
| [5] | 郭春兴,高培伟,耿飞,项红超.掺硅灰和粉煤灰混凝土抗氯离子渗透性[J].低温建筑技术,2010(03):7-9. |
| [6] | 张云升,孙伟,郑克仁,贾艳涛.水泥-粉煤灰浆体的水化反应进程[J].东南大学学报（自然科学版）,2006(01):118-123. |
| [7] | B. W. Langan;K. Weng;M. A. Ward .Effect of silica fume and fly ash on heat of hydration of Portland cement[J].Cement and Concrete Research,2002(7):1045-1051. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%