Effect of Curing Regime on Polymerization of C-S-H in Hardened Cement Pastes

^1, , ^2, , ^3, , ^4,

1.School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

2.School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

3.School of Materials Science and Engineering, Hebei United University, Tangshan 063009, China

4.School of Materials Science and Engineering, Hubei University, Wuhan 430062, China

基金项目: the Major State Basic Research Development Program of China (973 Program) (2009CB623201)

1.School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

2.School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

3.School of Materials Science and Engineering, Hebei United University, Tangshan 063009, China

4.School of Materials Science and Engineering, Hubei University, Wuhan 430062, China

[1]	A.V. Girao;I.G. Richardson;R. Taylor;R.M.D. Brydson .Composition, morphology and nanostructure of C-S H in 70% white Portland cement-30% fly ash blends hydrated at 55 ℃.[J].Cement and Concrete Research,2010(9):1350-1359.
[2]	I. Elkhadiri;F. Puertas .The effect of curing temperature on sulphate-resistant cement hydration and strength[J].Construction and Building Materials,2008(7):1331-1341.
[3]	A. Cwirzen .The effect of the heat-treatment regime on the properties of reactive powder concrete[J].Advances in Cement Research,2007(1):25-33.
[4]	Pipat Termkhajornkit;Remi Barbarulo .Modeling the coupled effects of temperature and fineness of Portland cement on the hydration kinetics in cement paste[J].Cement and Concrete Research,2012(3):526-538.
[5]	阎培渝,王强.变温条件下粉煤灰对混凝土抗压强度的影响[J].混凝土,2008(03):1-3.
[6]	I.G.Richardson .The nature of C-S-H in hardened cements[J].Cement and Concrete Research,1999(8):1131-1147.
[7]	Morten Daugaard Andersen;Hans J. Jakobsen;Jorgen Skibsted .Characterization of white Portland cement hydration and the C-S-H structure in the presence of sodium aluminate by ~(27)Al and ~(29)Si MAS NMR spectroscopy[J].Cement and Concrete Research,2004(5):857-868.

上一张下一张

计量

作者相关

文章评分

材料期刊网