The stress corrosion cracking(SCC) behaviour of 7A52 aluminum alloy in air and in 3.5％NaCl solution was researched by slow strain rate test(SSRT) and SEM-EDS.The SCC susceptibility was estimated with the loss of the reduction in area.The experimental results indicate that the SCC susceptibility of 7A52 aluminum alloy in 3.5％ chloride solution is the highest at strain rate of 1 × 10-6 s-1.The lowest one is under the condition of 1 × 10-5 s-1.Stress concentration and anode dissolving around Al-Fe-Mn intermetallics initiate micropores which will result in microcracks.The existence of intermetallics in the microstructure may play an important role in understanding the SCC initiation mechanisms of 7A52 aluminum alloy.
参考文献
| [1] | 刘继华,李荻,朱国伟,刘培英.7075铝合金应力腐蚀敏感性的SSRT和电化学测试研究[J].腐蚀与防护,2005(01):6-9. |
| [2] | 郑强,陈康华,黄兰萍,胡化文.高温预析出和固溶温度对7A52合金应力腐蚀开裂的影响[J].金属热处理,2005(07):14-17. |
| [3] | Davoodi A;Pan J;Leygraf C;Norgren S .The role of intermetallic particles in localized corrosion of an aluminum alloy studied by SKPFM and integrated AFM/SECM[J].Journal of the Electrochemical Society,2008(5):C211-C218. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%