The effect of pre-corrosion on fatigue behavior of high strength steel 38CrMoAl was investigated with a fatigue test method using the accelerated pre-corrosion specimen in the neutral salt spray environment.The methods of weight-loss and energy dispersive spectrum(EDS)were adopted.The corrosion weight-loss rate was fitted with the test time using power law,and the relationship between the corrosion weight-loss rate and the time was formulated.Moreover,the fatigue behaviors of the steel for different pre-corrosion time were investigated by the axis-direction tensile fatigue test.The fatigue life distribution characteristics of the pre-corrosion specimens were studied using the statistical probability methods,and the mathematical expectations and the standard tolerances of the material fatigue lives after different pre-corrosion time were obtained.It was found that the crack initiation of the high strength steel was accelerated by the preferential corrosion at the local plastic deform areas.The fatigue life obeys the lognormal distribution perfectly.Furthermore,within the common time range of the engineering,the standard tolerances of the logarithm of the fatigue life were independent of the pre-corrosion time.
参考文献
| [1] | 张建宇,费斌军.腐蚀环境下多裂纹结构的概率损伤容限分析[J].北京航空航天大学学报,2002(02):202-204. |
| [2] | S. Ishihara;Z. Y. Nan;A. J. McEvily;T. Goshima;S. Sunada .On the initiation and growth behavior of corrosion pits during corrosion fatigue process of industrial pure aluminum[J].International Journal of Fatigue,2008(9):1659-1668. |
| [3] | 赵海军,金平,柳文林,杨晓华.预腐蚀疲劳寿命影响系数模型研究[J].腐蚀科学与防护技术,2006(04):265-267. |
| [4] | 贺小帆,刘文珽,王忠波,杨洪源,王磊.预腐蚀对疲劳寿命分布特性及参数影响的初步研究[J].航空材料学报,2007(06):21-26. |
| [5] | 陈群志,杨蕊琴,李国元,王逾涯.腐蚀对30CrMnSiNi2A钢结构疲劳寿命的影响[J].装备环境工程,2007(05):7-9,17. |
| [6] | K. van der Walde;B. M. Hillberry .Characterization of pitting damage and prediction of remaining fatigue life[J].International Journal of Fatigue,2008(1):106-118. |
| [7] | Tong WP;Han Z;Wang LM;Lu J;Lu K .Low-temperature nitriding of 38CrMoAl steel with a nanostructured surface layer induced by surface mechanical attrition treatment[J].Surface & Coatings Technology,2008(20):4957-4963. |
| [8] | Shangguan Qianqian;Cheng Xianhua .Effect of Rare Earth Elements on Erosion Resistance of Nitrocarburized Layers of 38CrMoAl Steel[J].Journal of Rare Earths,2004(3):406-409. |
| [9] | Li S;Jung S;Park KW;Lee SM;Kim YG .Kinetic study on corrosion of steel in soil environments using electrical resistance sensor technique[J].Materials Chemistry and Physics,2007(1):9-13. |
| [10] | R.E. Melchers .A New Interpretation Of The Corrosion Loss Processes For Weathering Steels In Marine Atmospheres[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(12):3446-3454. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%