The effect of sodium hydroxide (NaOH) amount on phosphogypsum based cement was investigated. The mechanical performances and hydration mechanism of the phosphogyp-sum-based cement with different proportions of NaOH and steel slag were analyzed based on setting time, volume stability, strength test, XRD and SEM analyses. The experimental results show that, NaOH as an alkali activator significantly reduces the cement setting time and improves the cement early strength. But the acceleration of hydration proces produces coarse crystalline hydration products and the osteoporosis structure of hardened paste, which has a negative effect on later age strength. The combination of 1% NaOH and 5% steel slag as alkali activating agents is optimal with respect to early and later age strengths. Overdose of NaOH not only decreases the cement strength at later age, but also may cause problem of volume stability.
参考文献
| [1] | J.H. Potgieter;S.S. Potgieter;R.I. McCrindle: .A comparison of the performance of various synthetic gypsums in plant trials during the manufacturing of OPC clinker[J].Cement and Concrete Research,2004(12):2245-2250. |
| [2] | Manjit Singh .Treating waste phosphogypsum for cement and plaster manufacture[J].Cement and Concrete Research,2002(7):1033-1038. |
| [3] | 林宗寿,黄赘.磷石膏基免煅烧水泥的开发研究[J].武汉理工大学学报,2009(04):53-55,62. |
| [4] | 林宗寿,黄贇.碱度对磷石膏基免煅烧水泥性能的影响[J].武汉理工大学学报,2009(04):132-135. |
| [5] | Vladimir Zivica .Effects of type and dosage of alkaline activator and temperature on the properties of alkali-activated slag mixtures[J].Construction and Building Materials,2007(7):1463-1469. |
| [6] | A. Gruskovnjak;B. Lothenbach;F. Winnefeld .Hydration mechanisms of super sulphated slag cement[J].Cement and Concrete Research,2008(7):983-992. |
| [7] | S.Song;H.M.Jenniings .Pore solution chemistry of alkali-activated ground granulated blast-furnace slag[J].Cement and Concrete Research,1999(2):159-170. |
| [8] | Caijun Shi .Characteristics and cementitious properties of ladle slag fines from steel production[J].Cement and Concrete Research,2002(3):459-462. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%