Arc spraying with the cored wires was applied to deposit FeMnCr/Cr3C2 coatings on low carbon steel substrates, namely FM1, FM2 and FM3. Thermal shock resistances of the coatings were investigated to assess the influence of Cr3C2 content on thermal shock resistance. Characteristics of the coatings under thermal cycling test were studied by optical microscopy, field emission scanning electron microscope (FE-SEM) and energy dispersion spectrum (EDS), X-ray diffraction (XRD). The experimental results show that hardness of the coatings increases, bonding strength decreases slightly with increase of the Cr3C2 content of the coatings. As a result, FM2 coating possesses the best thermal shock resistance, attributing to its better thermal expansion matches and wettability than those of FM3 coating, less oxide rate than that of FM1 coating restraining from cracks formation and propagation in coatings.

参考文献

[1] Shao-Guang Liu;Jin-Ming Wu;Sheng-Cai Zhang;Shu-Jie Rong;Zhi-Zhang Li .High temperature erosion properties of arc-sprayed coatings using various cored wires containing Ti-Al intermetallics[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2007(5/6):555-561.
[2] B. Q. Wang;M. W. Seitz .Comparison in erosion behavior of iron-base coatings sprayed by three different arc-spray processes[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2001(1):755-761.
[3] Hjornhede A;Nylund A .Adhesion testing of thermally sprayed and laser deposited coatings[J].Surface & Coatings Technology,2004(2/3):208-218.
[4] M. A. Uusitalo;P. M. J. Vuoristo;T. A. Mantyla .Elevated temperature erosion-corrosion of thermal sprayed coatings in chlorine containing environments[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2002(7/8):586-594.
[5] XU Weipu,XU Binshi,ZHANG Wei,WU Yixiong.Erosion-Corrosion Behaviors of High Velocity Arc Sprayed Fe-Al/Cr3C2 Coating[J].武汉理工大学学报(材料科学版)英,2006(03):29-31.
[6] Q.M. Wang;Y.J. Tang;M.H. Guo .Thermal shock cycling behavior of NiCoCrAlYSiB coatings on Ni-base superalloys. I. Accelerated oxidation attack[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):337-349.
[7] Irisawa T;Matsumoto H .Thermal shock resistance and adhesion strength of plasma-sprayed alumina coating on cast iron[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2006(1/2):141-144.
[8] 徐维普,徐滨士,张伟,孟凡军,李新.高速电弧喷涂Fe-Al/Cr3C2粉芯丝材的研制与性能研究[J].兵器材料科学与工程,2004(02):43-45.
[9] Y. Wang;W. Tian;Y. Yang .Thermal shock behavior of nanostructured and conventional Al2O3/13 wt%TiO2 coatings fabricated by plasma spraying[J].Surface & Coatings Technology,2007(18):7746-7754.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%