Influence of Thickness on the Properties of Solution-derived LiMn_2O

武汉理工大学学报-材料科学版(英文版), 2009, 24(5): 706-710. doi: 10.1007/s11595-009-5706-0

^1, , ^2, , ^3, , ^4, , ^5,

1.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

2.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

3.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

4.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

5.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

基金项目: the Scientific Research Fund of Hunan Provincial Education Department(07B060)

Influence of Thickness on the Properties of Solution-derived LiMn_2O_4 Thin Films

WU Xianming ^1, , CHEN Shang ^2, , HE Zeqiang ^3, , MA Mingyou ^4, , LIU Jianben ^5,

1.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

2.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

3.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

4.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

5.College of Chemistry and Chemical Engineering,Jishou University,Jishou 416000,China

Keywords： lithium manganese oxides

LiMn_2O_4 thin films of different thickness were derived from solution deposition and heat treated by rapid thermal annealing.The phase identification and surface morphology were studied by X-ray diffraction and scanning electron microscopy.The electrochemical properties of the films were examined by galvanostatic charge-discharge experiments and electrochemical impedance spectroscopy.LiMn_2O_4 thin films of different thickness derived from solution deposition and rapid thermal annealing are homogeneous and crack free with the grain size between 20 nm and 50 nm.The specific capacity of these films is between 42 and 47μAh·cm~2·μm~(-1).The capacity decreases with the increase of discharge current density.The capacity loss per cycle increases from 0.012%to 0.16%after being cycled 50 times as the film thickness increases from 0.18μm to 1.04μm.The lithium diffusion coefficients of these films are in the same order of 10~(-11)cm~2·s~(-1).

参考文献

[1]	Han-Ki Kim;Tae-Yeon Seong;Young Soo Yoon .Characteristics of rapid-thermal-annealed LiNi_(1-x)Co_xO_2 cathode films for all-solid-state rechargeable thin film microbatteries[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2004(1):619-625.
[2]	Woon-Gi Choi;Soon-Gil Yoon .Structural and electrical properties of LiCoO_2 thin-film cathodes deposited on planar and trench structures by liquid-delivery metalorganic chemical vapour deposition[J].Journal of Power Sources,2004(2):236-241.
[3]	Cheng-Lung Liao;Yueh-Hsun Lee;Ho-Chieh Yu;Kuan-Zong Fung .Structure characterization and electrochemical properties of RF sputtered lithium nickel cobalt oxide thin films[J].Electrochimica Acta,2004(2/3):461-466.
[4]	Hee-Soo Moon;Jong-Wan Park .Improvement of cyclability of LiMn_2O_4 thin films by transition-metal substitution[J].Journal of Power Sources,2003(119/121):717-720.
[5]	S. B. Tang;M. O. Lai;L. Lu .Properties of nano-crystalline LiMn{sub}2O{sub}4 thin films deposited by pulsed laser deposition[J].Electrochimica Acta,2006(3):1161-1168.
[6]	A. Funabiki;M. Inaba;Z. Ogumi' S. -i. Yuasa;J. Otsuji;A. Tasaka .Impedance study on the electrochemical lithium intercalation into natural graphite powder[J].Journal of the Electrochemical Society,1998(1):172-178.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Influence of Thickness on the Properties of Solution-derived LiMn_2O_4 Thin Films

参考文献