The curing process of epoxy asphalt was analyzed by Fourier transform infrared (FT-IR)spectroscopy.Effect of curing temperature on viscosity of epoxy asphalt,and changes of mechanical properties with curing time were investigated.The evolution of concentration of epoxy band was followed as a function of the applied curing process.The experimental results indicate that the curing reaction rate of epoxy asphalt is invariable before 70 min at 120℃,and it decreases when curing time exceeds 70 min.The viscosity of epoxy asphalt increases slowly with curing time at initial curing stage.But it increases quickly after initial curing stage and the initial curing time decreases as the curing temperature increases.The tensile strength increases slowly at incipient curing stage and increases rapidly when curing time is form 20 min to 70 min.The elongation at break shows a decrease with curing time,but it exceeds 200%after cured.
参考文献
| [1] | Ronaldo C. Battista;Michele S. Pfeil;Eliane M.L. Carvalho .Fatigue life estimates for a slender orthotropic steel deck[J].Journal of Constructional Steel Research,2008(1):134-143. |
| [2] | Maria Castro .Structural design of asphalt pavement on concrete bridges[J].Canadian Journal of Civil Engineering,2004(4):695-702. |
| [3] | Giovanni Polacco;Jiri Stastna;Dario Biondi .Relation between polymer architecture and nonlinear viscoelastic behavior of modified asphalts[J].Current opinion in colloid & interface science,2006(4):230-245. |
| [4] | Yetkin Yildirim .Polymer modified asphalt binders[J].Construction and Building Materials,2007(1):66-72. |
| [5] | Polacco G;Berlincioni S;Biondi D;Stastna J;Zanzotto L .Asphalt modification with different polyethylene-based polymers[J].European Polymer Journal,2005(12):2831-2844. |
| [6] | Wen G.;Zhang Y.;Zhang YX.;Sun K.;Fan YZ. .Rheological characterization of storage-stable SBS-modified asphalts[J].Polymer Testing,2002(3):295-302. |
| [7] | Qian Zhendong;Luo Sang;Wang Jianwei .Laboratory evaluation of epoxy resin modified asphalt mixtures[J].Journal of Southeast University,2007(1):117-121. |
| [8] | 宗海,王建伟,吕斌.时温对环氧沥青混合料的影响分析[J].公路,2006(11):135-139. |
| [9] | J.Lamontagne;P.Dumas;V.Mouillet .Comparison by Fourier transform infrared (FTIR) spectroscopy of different ageing technqiues: application to road bitumens[J].Fuel,2001(4):483-488. |
| [10] | M. Sanchez-Soto;P. Pages;T. Lacorte;K. Briceno;F. Carrasco .Curing FTIR study and mechanical characterization of glass bead filled trifunctional epoxy composites[J].Composites science and technology,2007(9):1974-1985. |
| [11] | Karayannidou EG;Achilias DS;Sideridou ID .Cure kinetics of epoxy-amine resins used in the restoration of works of art from glass or ceramic[J].European Polymer Journal,2006(12):3311-3323. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%