Freeze-thaw durabilities of three types of concretes-normal portland cement concrete (OPC),high strength concrete (HSC) and steel fiber reinforced high strength concrete (SFRHSC)were systemically investigated under the attacks of chemical solution,and combination of external flexural stress and chemical solution.Four kinds of bitterns from salt lakes in Sinkiang,Qinghai,Inner Mongolia and Tibet provinces of China were used as chemical attack solutions.The relative dynamic modulus (RDM) was used as an index for evaluating the damage degree during the course of chemical attack and stress corrosion.The experimental results show that the freeze-thaw durability of concrete is visibly reduced in the present of the flexural stress,i e,stress accelerates the damage process.In order to quantify the stress accelerated effect,a stress accelerating coefficient was proposed.The stress accelerating coefficient is closely related with the types of bitterns and the numbers of freeze-thaw cycles is.The more numbers of freeze-thaw cycles is,the greater the stress accelerating coefficient for various concretes will be.In addition,there also exists a critical ratio of external stress to the maximum flexural stress.If the stress ratio exceeds the critical one,the freeze-thaw durability of various concretes will be greatly decreased compared to the responding concretes without applied stress.The critical stress ratio of OPC,HSC and SFRHSC is 0.30,0.40 and 0.40,respectively,indicating that HSC and SFRHSC have advantages over OPC and are suitable to use in the bittern erosion regions.
参考文献
| [1] | Aitcin P C;Pigeon M;Pleau R.Freezing and Thawing Durability of High Performance Concrete[A].Quebec:Concrete Canada,1998:383-391. |
| [2] | Mehta P K .Studies on Chemical Resistance of Low Water-cement Ratio Concretes[J].Cement and Concrete Research,15(06):969-978. |
| [3] | Janssen D J;Snyder M B.Mass Loss Experience with ASTM C666:with and without Deicing Salt[A].Québec City,Canada,1997:247-258. |
| [4] | Mu Ru;Miao Changwen;Liu Jiaping .Properties of Concrete Subjected to Freezing and Thawing under Sulphate Attack[J].Indian Concrete Journal,2001,75(07):451-454. |
| [5] | Mu Ru;Miao Changwen;Breugel K V.Properties of Air-entrained Concrete Subjected to Freeze-thaw Cycles and Salt Attack Simultaneously[A].江苏徐州:982-988. |
| [6] | 慕儒,缪昌文,刘加平,孙伟.氯化钠、硫酸钠溶液对混凝土抗冻性的影响及其机理[J].硅酸盐学报,2001(06):523-529. |
| [7] | 余红发,孙伟,武卫锋,杨山,鄢良慧.普通混凝土在盐湖环境中的抗卤水冻蚀性与破坏机理研究[J].硅酸盐学报,2003(08):763-769. |
| [8] | 余红发,孙伟,鄢良慧,杨波.在盐湖环境中高强与高性能混凝土的抗冻性[J].硅酸盐学报,2004(07):842-848. |
| [9] | 余红发,孙伟,鄢良慧,王晴.引气混凝土在中国盐湖环境中抗冻性的研究[J].武汉理工大学学报,2004(03):15-18. |
| [10] | Zhou Yixia;Cohen M D;Dolch L W .Effect of External Loads on the Frost-resistant Properties of Mortar with and without Silica Fume[J].ACI Materials Journal,1994,91(06):595-601. |
| [11] | W.Sun;Y.M.Zhang .Damage and damage resistance of high strength concrete under the action of load and freeze-thaw cycles[J].Cement and Concrete Research,1999(6):1519-1523. |
| [12] | Zivica V;Szabo V .The Behaviour of Cement Composite under Compression Load at Sulphate Attack[J].Cement and Concrete Research,1994,24(08):1475-1484. |
| [13] | Schneider U;Nagele E .Stress Corrosion of Cement Mortars in Ammonium Sulfate Solution[J].Cement and Concrete Research,1993,23(01):13-19. |
| [14] | Schneider U;Chen S W .Modeling and Empirical Formulas for Chemical Corrosion and Stress Corrosion of Cementitious Materials[J].Materials and Structures,1998,31(10):662-668. |
| [15] | Schneider U;Chert S W .The Chemomechanical Effect and the Mechanochemical Effect on High-performance Concrete Subjected to Stress Corrosion[J].Cement and Concrete Research,1998,28(04):509-522. |
| [16] | Schneider U;Chen S W .Behaviour of High-performance Concrete under Ammonium Nitrate Solution and Sustained Load[J].ACI Materials Journal,1999,96(01):47-51. |
| [17] | 余红发,孙伟,刘连新,翁智财,陈浩,李美丹.在盐湖卤水环境中混凝土应力腐蚀行为[J].哈尔滨工业大学学报,2007(12):1965-1968. |
| [18] | Wei Sun;Ru Mu;Xin Luo .Effect of chloride salt, freeze-thaw cycling and externally applied load on the performance of the concrete[J].Cement and Concrete Research,2002(12):1859-1864. |
| [19] | Sun Wei;Yu Hongfa;Wang Qing et al.Effect of Flexural Stress on Bittern Freezing-thawing Durability of Concrete Eexposed to Salt Lakes[J].J Wuhan Uni Tech,2005,27(07):46-49. |
| [20] | 余红发,慕儒,孙伟,缪昌文.弯曲荷载、化学腐蚀和碳化作用及其复合对混凝土抗冻性的影响[J].硅酸盐学报,2005(04):492-499. |
| [21] | Ababneh A N .The Coupled Effect of Moisture Diffusion,Chloride Penetration and Freezing-thawing on Concrete Durability[D].Denver:University of Colorado,2002. |
| [22] | 慕儒,严安,孙伟.荷载与冻融同时作用下HSC和SFRHSC的耐久性[J].工业建筑,1998(08):11-14. |
| [23] | Yu Hongfa .Study on High Performance Concrete in Salt Lake:Durability,Mechanism and Service Life Prediction[D].南京:东南大学,2004. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%