A simple technique was developed to join C/C composite to Cu using active Cu-3.5Si braze for nuclear thermal applications. The brazing alloy exhibited good wettability on C/C substrate due to the reaction layer formed at the interface. A strong interfacial bond of the brazing alloy on C/C with the formation of TiC + SiC + Ti5Si3 reaction layer was obtained. The produced CC/Cu/CuCrZr joint exhibited shear strength as high as 79 MPa and excellent thermal resistance during the thermal shock tests. (c) 2011 Elsevier B.V. All rights reserved.