Effect of Polyvinyl Alcohol with a Thiol End Group on the Properties of Polyacrylic Dispersions and Spray-dried Powder

武汉理工大学学报-材料科学版(英文版), 2007, 22(2): 261-265.

^1, , ^2, , ^3, , ^4,

1.Institute of Chemical Engineering, South China University of Technology, Guangzhou 510640, China

2.Institute of Chemical Engineering, South China University of Technology, Guangzhou 510640, China

3.Institute of Chemical Engineering, South China University of Technology, Guangzhou 510640, China

4.Institute of Chemical Engineering, South China University of Technology, Guangzhou 510640, China

Effect of Polyvinyl Alcohol with a Thiol End Group on the Properties of Polyacrylic Dispersions and Spray-dried Powder

The emulsion polymerization of highly shear-stable copolymer dispersions of methyl methacrylate and butyl acrylate were carried out using poly (vinyl alcohol) with a thiol end group (PVA-SH) as protective colloid. The dispersions can be transformed into corresponding redispersible powder via a spray dryingcooling process. On-line FT-IR monitoring shows that grafting polymer of PVA-g-PMMA was formed mainly at the stage-1 of the emulsion polymerization. TEM images show, the PVA-SH shell was fragmentary when adding SDS at initial stage and integrated when adding at particle growing or final stage. The particle size turns to be smaller when delayed adding SDS surfactant. Triethanolamine, a co-regulator of PVA-SH, controlled the Mn to 50 000-70 000 and reduced the PDI to 1.5-1.7. The acrylic dispersions with 0.8wt%-1.5wt% PVA-SH1 can be spray-dried into super dispersible polymer powder (SDPP), which can easily disperse in water and form reconstituted dispersions with an average particle size smaller than 1 micron.

参考文献

[1]	Guziak L F;Maclay W N .Redispersible Latex Polymer[J].Journal of Applied Polymer Scinece,1963,7:2249-2258.
[2]	Saija Leo M.;Uminski Maciej .Water-Redispersible Low-T_g Acrylic Powders for the Modification of Hydraulic Binder Compositions[J].Journal of Applied Polymer Science,1999(11):1781-1787.
[3]	Yoshihiko Ohama .Polymer-based Admixtures[J].Cement & concrete composites,1998(2/3):189-212.
[4]	Yuki K .The Role of Polyvinyl Alcohol in Emulsion Polymerization[J].Polymer International,1993,30:513-517.
[5]	Miyazaki H.;Sato T.;Maruyama H.;Okaya T.;Terada K. .EFFECT OF POLY(VINYL ACETATE/VINYL ALCOHOL) COPOLYMER WITH A THIOL END GROUP AS A STERIC STABILIZER ON DISPERSION POLYMERIZATION OF STYRENE[J].Journal of Applied Polymer Science,1996(12):2149-2157.
[6]	Takuji Okaya;Atsushi Suzuki;Kenji Kikuchi .Effect of Additive on the Initial Stage of Emulsion Polymerization of Methyl Methacrylate using Polyvinyl Alcohol as a Protective Colloid[J].Macromolecular Symposium,2000,150:143-148.
[7]	Takuji Okaya;Atsushi Suzuki;Kenji Kikuchi .Importance of grafting in the emulsion polymerization of MMA using PVA as a protective colloid. Effect of initiators[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,1999(1/3):123-125.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Effect of Polyvinyl Alcohol with a Thiol End Group on the Properties of Polyacrylic Dispersions and Spray-dried Powder

参考文献